JIS G3116 Grade SG325
Equivalent material: GOST 18K, GOST 14G2, GOST 14Г2, GOST 10G2B, AS 7-430R, AS 7-430N, AS 7-430T, AS 7-430A, EN P295GH, NF A48AP, BS 151-430, BS 154-430, BS 161-430, BS 223-460, BS 225-460, UNI Fe510-1KG, UNI Fe510-1KT, UNI Fe510-1KW, UNI Fe510-2KG, UNI Fe510-2KT, UNI Fe510-2KW, ÖNORM 17Mn4KW, ASTM E, JIS SG365, EN P235GH, DIN HI, NF A37CP, NF A37AP, BS 141-360, BS 151-360, BS 154-360, BS 161-360, BS 164-360, ÖNORM St35KW, UNE A37 Gr.RCI, UNE A37 Gr.RAII, SIS 1330, ASTM A, ASTM 65 [450], JIS SPV450, JIS SPV490, DIN 17Mn4, ASTM C, ASTM WPC, DIN 1.0437, DIN TTSt 41, DIN P310NB, AFNOR BS3, AFNOR P310NB, BS P310NB, EN P310NB, EN 1.0437, GB/T HP325, GB/T L13258, ASTM Grade WPL6, UNS K02104, UNS K02100, UNS K03009, DIN 1.0477, DIN P285NH, AFNOR P285NH, BS P285NH, EN P285NH, EN 1.0477, ISO P28, ISO PH28, ISO PT450GH
JIS G3116 Grade SG325 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3116 Grade SG325 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3116 Grade SG325 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3116 Grade SG325 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3116 Grade SG325 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 22 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 490 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 325 MPa |
- |