JIS G4303 Grade SUS836L solution treated
Equivalent material: ASTM S32053, ASTM F70, UNS S32053
JIS G4303 Grade SUS836L solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 8.8 g/cm³ |
Typical for Nickel Steel |
JIS G4303 Grade SUS836L solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Melting point |
- |
Melting point of 1316 - 1595 °C |
Typical for Nickel Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 456 J/(kg·K) |
Typical for Nickel Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 10 - 50 W/(m·K) |
Typical for Nickel Steel |
JIS G4303 Grade SUS836L solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Nickel Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 35 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 217 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 96 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 230 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Nickel Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 40 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 76 GPa |
Typical for Nickel Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |