JIS G4303 Grade SUS416 quenched and tempered
Equivalent material: GB Y1Cr13, AS 416, NF Z12CF13, NF Z11CF13, BS 416S21, BS 416S29, BS 416S37, UNI X12CrS13, EN X12CrS13, UNE X12CrS13, SIS 2380-02, SIS 2380-03, SIS 2380, AMS 5610, ASME 416, ASTM 416, ASTM 6F with S, ASTM 6F with Se, MIL 416, AISI 416, SAE 51416, GB/T Y1Cr13, GB/T Y1Cr13-Q, DIN 1.4005, DIN X12CrS13, AFNOR Z11CF13, AFNOR X12CrS13, BS X12CrS13, AISI 51416, AISI S41600, SAE 416, SAE S41600, EN 1.4005, ASTM Grade 6F (416), UNS S41600, AFNOR Z12C13M, AISI 410, SAE 410, GOST 12CH13, ASTM F6a-1, ASTM F6a Class 1, UNS S41000
JIS G4303 Grade SUS416 quenched and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G4303 Grade SUS416 quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G4303 Grade SUS416 quenched and tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G4303 Grade SUS416 quenched and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 17 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 159 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 540 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 345 MPa |
- |