AISI 416 Annealed
Equivalent material: DIN 1.4005, DIN X12CrS13, AFNOR Z11CF13, AFNOR X12CrS13, BS 416S21, BS X12CrS13, AISI 51416, AISI S41600, SAE 51416, SAE 416, SAE S41600, JIS SUS416, EN X12CrS13, EN 1.4005, GB Y1Cr13, ASTM 416, ASTM Grade 6F (416), UNS S41600
AISI 416 Annealed general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.7 g/cm³ |
AISI 416 Annealed thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.9E-6 1/K |
| Melting point |
- |
Melting point of 1480 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 30 W/(m·K) |
AISI 416 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.15 % |
| Chromium |
Chromium of 12 - 14 % |
| Iron |
Iron of 82.4 - 87.9 % |
| Manganese |
Manganese of 0 - 1.5 % |
| Molybdenum |
Molybdenum of 0 - 0.6 % |
| Phosphorus |
Phosphorus of 0 - 0.06 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0.15 - 0.35 % |
AISI 416 Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
AISI 416 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 32 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 300 MPa |
- |