AISI 410 Hardened
Equivalent material: DIN 1.4006, DIN X10Cr13, DIN X12Cr13, DIN GX10Cr13, AFNOR Z10C13, AFNOR Z13C13, AFNOR Z6C13, BS 410S21, UNI X12Cr13, SS 2302, UNE F.3401, SAE 410, JIS SUS410, JIS SUS410TKA, JIS SUS410TKC, EN X12Cr13, EN 1.4006, ISO X10Cr13, ISO C1, GOST 12Ch13, ASTM MT410, ASTM 410, ASTM TP410, ASTM Grade CPCA15, UNS S41000, ASTM F6, ASTM Grade F6, ASTM S41000, AFNOR Z12C13M, JIS SUS416, GOST 12CH13, ASTM F6a-1, ASTM F6a Class 1, ASTM Grade 6, ASTM Grade B6, ASTM Grade B6X, DIN 1.4024, DIN X15Cr13, AISI S41000, SAE S41000, JIS SUS410J1FB, JIS SUS410J1, JIS SUS410TB, JIS SUSF410B, JIS SUSF410C, JIS SUSF410A, JIS SUSF410D, EN X15Cr13, EN 1.4024, ISO X15Cr13
AISI 410 Hardened general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 410 Hardened thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 1/K |
| Melting point |
- |
Melting point of 1480 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 30 W/(m·K) |
AISI 410 Hardened chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 - 0.15 % |
| Chromium |
Chromium of 11.5 - 13.5 % |
| Iron |
Iron of 83.1 - 88.4 % |
| Manganese |
Manganese of 0 - 1.5 % |
| Nickel |
Nickel of 0 - 0.75 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 410 Hardened electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
AISI 410 Hardened mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 16 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 740 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 540 MPa |
- |