ASTM A268 Grade TP410 Reheated
Equivalent material: DIN 1.4006, DIN X10Cr13, DIN X12Cr13, DIN GX10Cr13, AFNOR Z10C13, AFNOR Z13C13, AFNOR Z6C13, BS 410S21, UNI X12Cr13, SS 2302, UNE F.3401, AISI 410, SAE 410, JIS SUS410, JIS SUS410TKA, JIS SUS410TKC, EN X12Cr13, EN 1.4006, ISO X10Cr13, ISO C1, GOST 12Ch13, ASTM MT410, ASTM 410, ASTM Grade CPCA15, UNS S41000, ASTM F6, ASTM Grade F6
ASTM A268 Grade TP410 Reheated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
ASTM A268 Grade TP410 Reheated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
ASTM A268 Grade TP410 Reheated chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 11.5 - 13.5 % |
| Manganese |
Manganese of 1 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A268 Grade TP410 Reheated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
ASTM A268 Grade TP410 Reheated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 207 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 95 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 415 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 205 MPa |
- |