DIN 17440 Grade X10Cr13 quenched and tempered (+QT)
DIN 17440 Grade X10Cr13 quenched and tempered (+QT) introduction
Application:
- normally in quenched and tempered state with fine grounded or polished surface (tap elements, valve spindle, arbor, pump elements, bolts, screws)
- application temperature: up to 550 °C
- for construction elements in water and steam an mild acting media in food inustry
Equivalent material: AS 410, AFNOR Z12C13, BS 410S21, GOST 12Ch13, ISO 3, UNI X12Cr13, JIS SUS410, PN 1H13, SS 2302, UNE F.3401, UNE X12Cr13, ASTM 410, DIN X12Cr13, DIN 1.4006, DIN GX10Cr13, AFNOR Z10C13, AFNOR Z13C13, AFNOR Z6C13, AISI 410, SAE 410, JIS SUS410TKA, JIS SUS410TKC, EN X12Cr13, EN 1.4006, ISO X10Cr13, ISO C1, ASTM MT410, ASTM TP410, ASTM Grade CPCA15, UNS S41000
DIN 17440 Grade X10Cr13 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.7 - 7.73 g/cm³ |
DIN 17440 Grade X10Cr13 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.02E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.09E-5 - 1.1E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.13E-5 - 1.15E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.16E-5 - 1.2E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.22E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of 0 - 550 °C |
- |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 439 - 460 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 474 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 498 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 538 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 564 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 598 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 25.9 - 30 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 25.3 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 25.2 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 25.2 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 25.4 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 25.7 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 25.9 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 7.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 6.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 5.3 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.8 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.1 mm²/s |
- |
DIN 17440 Grade X10Cr13 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 - 0.12 % |
| Chromium |
Chromium of 12 - 14 % |
| Manganese |
Manganese of 1 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
DIN 17440 Grade X10Cr13 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 5.59E-7 - 6E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 6.4E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 7.32E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 8.17E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 8.97E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 9.74E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.05E-6 Ω·m |
DIN 17440 Grade X10Cr13 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
20.0 °C |
Elastic modulus of 216 - 217.99 GPa |
| - |
100.0 °C |
Elastic modulus of 213 - 215 GPa |
| - |
200.0 °C |
Elastic modulus of 188 - 207 GPa |
| - |
300.0 °C |
Elastic modulus of 164 - 200 GPa |
| - |
400.0 °C |
Elastic modulus of 188.79 - 192 GPa |
| Elongation |
20.0 °C |
Elongation of 15 - 18 % |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 12 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
| - |
100.0 °C |
Poisson's ratio of 0.29 [-] |
| - |
200.0 °C |
Poisson's ratio of 0.29 [-] |
| - |
300.0 °C |
Poisson's ratio of 0.31 [-] |
| - |
400.0 °C |
Poisson's ratio of 0.31 [-] |
| Shear modulus |
20.0 °C |
Shear modulus of 84.82 GPa |
| - |
100.0 °C |
Shear modulus of 82.5 GPa |
| - |
200.0 °C |
Shear modulus of 79.57 GPa |
| - |
300.0 °C |
Shear modulus of 75.86 GPa |
| - |
400.0 °C |
Shear modulus of 72 GPa |
| Tensile strength |
20.0 °C |
Tensile strength of 600 - 800 MPa |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 600 - 800 MPa |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 420 MPa |
| - |
50.0 °C |
Yield strength Rp0.2 of 430 MPa |
| - |
100.0 °C |
Yield strength Rp0.2 of 420 MPa |
| - |
150.0 °C |
Yield strength Rp0.2 of 410 MPa |
| - |
200.0 °C |
Yield strength Rp0.2 of 400 MPa |
| - |
250.0 °C |
Yield strength Rp0.2 of 382 MPa |
| - |
300.0 °C |
Yield strength Rp0.2 of 365 MPa |
| - |
350.0 °C |
Yield strength Rp0.2 of 335 MPa |
| - |
400.0 °C |
Yield strength Rp0.2 of 305 MPa |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 420 MPa |
Our steel products are engineered to deliver long-lasting performance, offering an excellent return on investment.