JIS G4307 Grade SUS410 cold-rolled, annealed, quenched and tempered
Equivalent material: GB 1Cr12, GB 1Cr13, GOST 12Х13, GOST 12H13, GOST 12H13-Sh, GOST 15H13L, AS 410, DIN X10Cr13, NF Z12C13, NF Z10C13, BS 410S21, BS 410S21-690, BS 410S21-720, BS 410S21-760, BS 410S21-750, BS 410S21-770, BS 410C21, UNI X12Cr13, UNI X10Cr13, UNI X12Cr13KG, UNI X12Cr13KW, EN X12Cr13, UNE X10Cr13, SIS 2302, GB/T 1Cr12, EN X8CrNi25-21, AMS 5521, AMS 5572, AMS 5577, AMS 5651, AMS 7490, ASME 310S, ASTM TP310S, ASTM 310S, ASTM MT310S, AISI 310S, ASTM CR310S, ASTM WP310S, SAE 310S, AS H3A, NF Z12CN13M, BS 420C29, UNI GX12Cr13, AMS 5351, ASTM CPCA15, ASTM CA15, ASTM CA15-A, ASTM CA15M-A, ASTM CA15-B, ASTM CA15-C, ASTM CA15-D, MIL Class 1, MIL 410, JIS SCS1, AS En56A, IS 12Cr13, SIS 2302-03, AMS 5504, AMS 5505, AMS 5591, AMS 5613, AMS 5776, AMS 5821, AMS 7493, ASME 6, ASME 410, ASTM TP410, ASTM 410, ASTM F6, ASTM 13Cr, ASTM F6a-1, ASTM 6, ASTM B6, ASTM F6a-2, ASTM F6a-3, ASTM F6a-4, ASTM B6X, ASTM MT410, JIS SUS410TB, JIS SUS410TKA, AISI 410, SAE 410, SAE 51410, ASTM 51, AISI S41001, JIS SUS410, ASTM Grade F6, UNS S41000, ASTM S41000, ASTM Grade 6, DIN 1.4006, AFNOR Z10C13, AFNOR Z13C13, SS 2302, UNE F.3401, JIS SUS410TKC, EN 1.4006, ISO X10Cr13, ISO C1, GOST 12Ch13, ASTM Grade CPCA15
JIS G4307 Grade SUS410 cold-rolled, annealed, quenched and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS410 cold-rolled, annealed, quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS410 cold-rolled, annealed, quenched and tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 11.5 - 13.5 % |
| Iron |
Iron of 83.68 - 88.5 % |
| Manganese |
Manganese of 1 % |
| Nickel |
Nickel of 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
JIS G4307 Grade SUS410 cold-rolled, annealed, quenched and tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS410 cold-rolled, annealed, quenched and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 20 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 441 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 206 MPa |
- |