JIS G4303 Grade SUS329J3L solution treated
Equivalent material: DIN 1.4462, DIN 22-5-3, DIN S31803, DIN X2CrNiMoN22-5-3, AFNOR Z3CND22-05Az, BS 318S13, SS 2377, AISI 2205, AISI S31803, AISI S32205, SAE 2205, SAE S31803, SAE S32205, JIS SUS329J3LTP, JIS SUS329J3LTB, EN X2CrNiMoN22-5-3, EN 1.4462, ISO 4462-318-03-I, GOST 02Ch22N5AM2, GB 022Cr22Ni5Mo3N, ASTM F 51, ASTM S31803, ASTM 4A, ASTM F 60, ASTM 2205, ASTM Grade F51, ASTM S32205, UNS S31803, UNS S32205
JIS G4303 Grade SUS329J3L solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Duplex Stainless Steel |
JIS G4303 Grade SUS329J3L solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 1/K |
Typical for Duplex Stainless Steel |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 502 J/(kg·K) |
Typical for Duplex Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 13 - 30 W/(m·K) |
Typical for Duplex Stainless Steel |
JIS G4303 Grade SUS329J3L solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
Typical for Duplex Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 18 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 302 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 32 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 320 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 40 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 620 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 450 MPa |
- |