EN 10217-7 Grade X2CrNiMoN22-5-3 solution annealed (+AT)
EN 10217-7 Grade X2CrNiMoN22-5-3 solution annealed (+AT) introduction
The austenitic ferritic steel X2CrNiMoN22-5-3 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 295 °C) also in the welded condition.
Equivalent material: GB 022Cr22Ni5Mo3N, GB S22253, UNS S31803, DIN 1.4462, DIN 22-5-3, DIN S31803, DIN X2CrNiMoN22-5-3, AFNOR Z3CND22-05Az, BS 318S13, SS 2377, AISI 2205, AISI S31803, AISI S32205, SAE 2205, SAE S31803, SAE S32205, JIS SUS329J3L, JIS SUS329J3LTP, JIS SUS329J3LTB, EN 1.4462, ISO 4462-318-03-I, GOST 02Ch22N5AM2, ASTM F 51, ASTM S31803, ASTM 4A, ASTM F 60, ASTM 2205, ASTM Grade F51, ASTM S32205, UNS S32205
EN 10217-7 Grade X2CrNiMoN22-5-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.8 g/cm³ |
EN 10217-7 Grade X2CrNiMoN22-5-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.3E-5 - 1.33E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 13.4 - 15 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 14.9 W/(m·K) |
- |
EN 10217-7 Grade X2CrNiMoN22-5-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 21 - 23 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3.5 % |
| Nickel |
Nickel of 4.5 - 6.5 % |
| Nitrogen |
Nitrogen of 0.1 - 0.22 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10217-7 Grade X2CrNiMoN22-5-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.85E-7 - 8E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 8.44E-7 Ω·m |
EN 10217-7 Grade X2CrNiMoN22-5-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 - 206 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 180 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 25 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 700 - 920 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 700 - 920 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 450 MPa |
- |
| - |
50.0 °C |
Yield strength Rp0.2 of 415 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 360 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 335 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 310 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 295 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 450 MPa |
- |