JIS G4051 Grade S10C
Equivalent material: GB 10, GOST 8, GOST 10, GOST 08, AS C1010, AS K1010, AS R1010, AS S1010, AS A1010, EN C10D, DIN C10, DIN Ck10, DIN D10-2, NF AF34C10, NF XC10, BS 045M10, BS 10HS, BS 10CS, BS 040A10, UNI C10, UNI 1C10, UNI 2C10, UNI 2C15, ÖNORM UGG12, ÖNORM UC12, ÖNORM RGG12, ÖNORM RC12, UNE C10K, UNE F.151, UNE F.151.A, SIS 1265-02, SIS 1265-11, SIS 1265-12, SIS 1265-16, SIS 1265, AMS 5040, ASTM 1010, ASTM M1010, ASTM MT1010, MIL 1010, AISI 1010, AISI MT1010, EN C10, SAE 1010, DIN St34-2, DIN St35, EN C10E, GB/T 10, GB/T 10, GB 10, DIN 1.0301, AFNOR C10, BS C10, JIS S09SK, EN HX340LAD, EN 1.0301, ISO CE10, GB/T U20102, UNS G10100, DIN 1.1121, DIN C10E, AFNOR C10RR, AFNOR XC 10, AFNOR C10E, BS En2A, BS En2B, BS 040A04, BS 040A12, BS C10E, BS En32A, SS 1264, JIS S09CK, JIS S12C, JIS SWRCH10K, JIS SWCH10K, EN HX300LAD, EN 1.1121, ISO C10, ISO C10E, ISO S10C, ASTM Grade 1010
JIS G4051 Grade S10C general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G4051 Grade S10C thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G4051 Grade S10C chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 - 0.13 % |
| Iron |
Iron of 98.85 - 99.47 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.035 % |
JIS G4051 Grade S10C magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G4051 Grade S10C electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G4051 Grade S10C mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |