DIN 17210 Grade Ck10 soft annealed (+A)
DIN 17210 Grade Ck10 soft annealed (+A) introduction
The steel Ck 10 is used for smaller wear loaded parts with low core strength in the vehicle and mechanical engineering as well as for parts of larger dimension and complexer shape as the base grade C 10 (e.g. pins, bushes, compression mouldings and stampings).
The lowest application amounts to -25 degrees C.
Equivalent material: NBN C10-2, CSN 12010, AFNOR XC10, BS 045M10, GOST 10, ISO C10, UNI 2C10, JIS S10C, SS 1265, VSM CK10, UNE F.1510-C10K, ASTM 1010, DIN C10E, DIN 1.1121, AFNOR C10RR, AFNOR XC 10, AFNOR C10E, BS 040A10, BS En2A, BS En2B, BS 040A04, BS 040A12, BS C10E, BS En32A, UNI C10, SS 1264, AISI 1010, SAE 1010, JIS S09CK, JIS S12C, JIS SWRCH10K, JIS SWCH10K, EN C10E, EN HX300LAD, EN 1.1121, ISO C10E, ISO S10C, GOST 08, GB 10, GB/T 10, GB/T U20102, ASTM M1010, ASTM Grade 1010, UNS G10100
DIN 17210 Grade Ck10 soft annealed (+A) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 17210 Grade Ck10 soft annealed (+A) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Max service temperature, long |
- |
Max service temperature, long of -25 - 0 °C |
- |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 57.5 - 58.7 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 54.4 - 55.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 50.2 - 51.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 47.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 43.4 - 44 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 39.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 36 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 15.9 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 14.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.8 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 9.2 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.6 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
DIN 17210 Grade Ck10 soft annealed (+A) chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 - 0.13 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
DIN 17210 Grade Ck10 soft annealed (+A) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
DIN 17210 Grade Ck10 soft annealed (+A) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.3E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 3.94E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.01E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.25E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.7E-7 Ω·m |
DIN 17210 Grade Ck10 soft annealed (+A) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
| - |
200.0 °C |
Elastic modulus of 193 - 199 GPa |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
Rely on our strong, dependable steel to support your most critical applications.