DIN 1652-3 Grade C10 cold drawn

DIN 1652-3 Grade C10 cold drawn

DIN 1652-3 Grade C10 cold drawn introduction

The steel C 10 is used for wear loaded parts with low core strength in the vehicle and mechanical engineering (e.g. pins, lever, compression mouldings and stampings).
The lowest application amounts to -25 °C, the best application from 5 to 10 mm nominal size.
As bright steel product it is used in the form of rods (bright, straight) in different conditions (see DIN EN 10277 : 1999-10).

Equivalent material: AFNOR XC10, BS 045M10, GOST 10, UNI 1C10, JIS S10C, PN 10, ASTM 1010, DIN 1.0301, AFNOR C10, BS C10, AISI 1010, SAE 1010, JIS S09SK, EN C10, EN HX340LAD, EN 1.0301, ISO CE10, GB/T 10, GB/T U20102, UNS G10100

DIN 1652-3 Grade C10 cold drawn general

Property Temperature Value
Density 20.0 °C Density of 7.85 g/cm³

DIN 1652-3 Grade C10 cold drawn thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.08E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.19E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.25E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.3E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.36E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.41E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.45E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.49E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Max service temperature, long - Max service temperature, long of -25 - 0 °C -
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 57.5 W/(m·K) -
- 100.0 °C Thermal conductivity of 55.7 W/(m·K) -
- 200.0 °C Thermal conductivity of 51.9 W/(m·K) -
- 300.0 °C Thermal conductivity of 47.6 W/(m·K) -
- 400.0 °C Thermal conductivity of 43.4 W/(m·K) -
- 500.0 °C Thermal conductivity of 39.6 W/(m·K) -
- 600.0 °C Thermal conductivity of 36 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 15.9 mm²/s -
- 100.0 °C Thermal diffusivity of 14.3 mm²/s -
- 200.0 °C Thermal diffusivity of 12.5 mm²/s -
- 300.0 °C Thermal diffusivity of 10.8 mm²/s -
- 400.0 °C Thermal diffusivity of 9.2 mm²/s -
- 500.0 °C Thermal diffusivity of 7.6 mm²/s -
- 600.0 °C Thermal diffusivity of 6.1 mm²/s -

DIN 1652-3 Grade C10 cold drawn chemical

Property Value
Carbon Carbon of 0.07 - 0.13 %
Manganese Manganese of 0.3 - 0.6 %
Phosphorus Phosphorus of 0.05 %
Silicon Silicon of 0.4 %
Sulfur Sulfur of 0.045 %

DIN 1652-3 Grade C10 cold drawn magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

DIN 1652-3 Grade C10 cold drawn electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 1.1E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.3E-7 Ω·m
- 200.0 °C Electrical resistivity of 3.04E-7 Ω·m
- 300.0 °C Electrical resistivity of 3.94E-7 Ω·m
- 400.0 °C Electrical resistivity of 5.01E-7 Ω·m
- 500.0 °C Electrical resistivity of 6.25E-7 Ω·m
- 600.0 °C Electrical resistivity of 7.7E-7 Ω·m

DIN 1652-3 Grade C10 cold drawn mechanical

Property Temperature Value Comment
Elastic modulus -100.0 °C Elastic modulus of 217 GPa -
- 20.0 °C Elastic modulus of 212 GPa -
- 100.0 °C Elastic modulus of 207 GPa -
- 200.0 °C Elastic modulus of 199 GPa -
- 300.0 °C Elastic modulus of 192 GPa -
- 400.0 °C Elastic modulus of 184 GPa -
- 500.0 °C Elastic modulus of 175 GPa -
- 600.0 °C Elastic modulus of 164 GPa -
Elongation 20.0 °C Elongation of 7 - 12 % -
Hardness, Brinell 20.0 °C Hardness, Brinell of 131 [-] -
Poisson's ratio 20.0 °C Poisson's ratio of 0.28 [-] -
Shear modulus 23.0 °C Shear modulus of 82 GPa Typical for Low Carbon Steel
Tensile strength 20.0 °C Tensile strength of 340 - 500 MPa -
Yield strength 20.0 °C Yield strength of 180 - 400 MPa -