EN 10132-2 Grade C10E soft annealed or soft annealed and skin passed (+A or +A+LC)
EN 10132-2 Grade C10E soft annealed or soft annealed and skin passed (+A or +A+LC) introduction
Cold-rolled narrow strip made of the mild steel C10E will be delivered in thicknesses up to 10 mm for case hardening in following conditions:
- soft annealed or soft annealed and little rerolled (+A or +LC),
- cold rolled (+CR).
Equivalent material: AS CA1010, GB 10, GB U20102, IS 10C4, ISO C10E, JIS S09CK, JIS S10C, GOST 08, GOST 10, KS SM9CK, KS SM10C, ASTM A568 Grade 1010, UNS G10100, SAE 1010, DIN Ck10, DIN 1.1121, DIN C10E, AFNOR C10RR, AFNOR XC 10, AFNOR C10E, BS 040A10, BS En2A, BS En2B, BS 040A04, BS 040A12, BS C10E, BS 045M10, BS En32A, UNI C10, SS 1264, AISI 1010, JIS S12C, JIS SWRCH10K, JIS SWCH10K, EN HX300LAD, EN 1.1121, ISO C10, ISO S10C, GB/T 10, GB/T U20102, ASTM 1010, ASTM M1010, ASTM Grade 1010
EN 10132-2 Grade C10E soft annealed or soft annealed and skin passed (+A or +A+LC) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10132-2 Grade C10E soft annealed or soft annealed and skin passed (+A or +A+LC) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 57.5 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 55.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 51.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 47.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 43.4 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 39.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 36 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 15.9 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 14.3 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.8 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 9.2 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.6 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6.1 mm²/s |
- |
EN 10132-2 Grade C10E soft annealed or soft annealed and skin passed (+A or +A+LC) chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 - 0.13 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10132-2 Grade C10E soft annealed or soft annealed and skin passed (+A or +A+LC) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10132-2 Grade C10E soft annealed or soft annealed and skin passed (+A or +A+LC) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.1E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.3E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 3.94E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.01E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.25E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.7E-7 Ω·m |
EN 10132-2 Grade C10E soft annealed or soft annealed and skin passed (+A or +A+LC) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 26 % |
- |
| Hardness, Rockwell B |
20.0 °C |
Hardness, Rockwell B of 73 [-] |
- |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 135 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 430 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 345 MPa |
- |