JIS G3468 Grade SUS329J1TPY
Equivalent material: DIN 1.4460, DIN X4CrNiMoN27-5-2, DIN X8CrNiMo27-5, DIN X3CrNiMoN27-5-2, AFNOR Z5CND27-05Az, BS X3CrNiMoN27-5-2, AISI 329, SAE 329, JIS SUS329J1TP, JIS SUS329J1TB, JIS SCS11, EN X3CrNiMoN27-5-2, EN 1.4460, ISO X3CrNiMoN27-5-2, ISO 4460-312-00-I, ISO DM34F, ISO 55, ASTM 329, ASTM Grade F50, UNS S32900
JIS G3468 Grade SUS329J1TPY general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Duplex Stainless Steel |
JIS G3468 Grade SUS329J1TPY thermal
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
Typical for Duplex Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 6 - 18 % |
- |
| Elongation A5, transverse |
23.0 °C |
Elongation A5, transverse of 13 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Duplex Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Duplex Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 590 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 390 MPa |
- |
JIS G3468 Grade SUS329J1TPY electrical
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 1/K |
Typical for Duplex Stainless Steel |
| Max service temperature |
- |
Max service temperature of 300 °C |
Typical for Duplex Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Duplex Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 - 502 J/(kg·K) |
Typical for Duplex Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 13 - 30 W/(m·K) |
Typical for Duplex Stainless Steel |
JIS G3468 Grade SUS329J1TPY mechanical
| Property |
Value |
| Wall thickness |
Wall thickness of 2 - 8 mm |