ASTM A694 Grade F50 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened
Equivalent material: ASTM Grade F50, DIN 1.4460, DIN X4CrNiMoN27-5-2, DIN X8CrNiMo27-5, DIN X3CrNiMoN27-5-2, AFNOR Z5CND27-05Az, BS X3CrNiMoN27-5-2, AISI 329, SAE 329, JIS SUS329J1TP, JIS SUS329J1TPY, JIS SUS329J1TB, JIS SCS11, EN X3CrNiMoN27-5-2, EN 1.4460, ISO X3CrNiMoN27-5-2, ISO 4460-312-00-I, ISO DM34F, ISO 55, ASTM 329, UNS S32900
ASTM A694 Grade F50 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A694 Grade F50 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
ASTM A694 Grade F50 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened chemical
| Property |
Value |
| Carbon |
Carbon of 0.3 % |
| Manganese |
Manganese of 1.6 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.025 % |
ASTM A694 Grade F50 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened magnetic
| Property |
Temperature |
Value |
Comment |
| Curie temperature |
20.0 °C |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A694 Grade F50 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A694 Grade F50 Normalized, Normalized and Tempered, Quenched and Tempered, or Precipitation Hardened mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 20 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 440 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 345 MPa |
- |