JIS G3313 Grade CR3
Equivalent material: DIN 1.0338, DIN St 14, DIN St14, DIN St 4, DIN DC04, AFNOR ES, AFNOR DC04, BS 1CR, BS 1CS, BS 1HR, BS 1HS, BS CR1, BS DC04, UNI FeP04, UNE AP04, JIS SPCE, JIS SPCF, EN DC04, EN FeP04, EN DC04, EN 1.0338, ISO CR3, ISO CR24, GOST 08JuA, GB/T 08F, GB/T U20080
JIS G3313 Grade CR3 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3313 Grade CR3 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3313 Grade CR3 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3313 Grade CR3 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3313 Grade CR3 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 35 % |
- |
| Elongation A80 |
23.0 °C |
Elongation A80 of 34 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 53 [-] |
- |
| Hardness, Rockwell Superficial 30-T |
23.0 °C |
Hardness, Rockwell Superficial 30-T of 52 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 350 MPa |
- |
Collaborate with us to harness the power of steel and unlock innovative solutions that drive progress and innovation.