ISO 16120-4 Grade C10D2
ISO 16120-4 Grade C10D2 introduction
Non-alloy steel wire rod for drawing and/or cold rolling with specific requirements for special applications (e.g. application for springs, steel wire).
Equivalent material: GB C10D2, ASTM A510 Grade 1010, UNS G10100, ISO C10D2, DIN 1.1114, DIN C10D2, AFNOR C10D2, BS C10D2, AISI 1010, SAE 1010, EN 1.1114, ASTM M1010, ASTM Grade 1010
ISO 16120-4 Grade C10D2 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ISO 16120-4 Grade C10D2 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ISO 16120-4 Grade C10D2 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.01 % |
| Carbon |
Carbon of 0.08 - 0.12 % |
| Chromium |
Chromium of 0.1 % |
| Copper |
Copper of 0.15 % |
| Manganese |
Manganese of 0.3 - 0.5 % |
| Molybdenum |
Molybdenum of 0.05 % |
| Nickel |
Nickel of 0.1 % |
| Nitrogen |
Nitrogen of 7E-3 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.3 % |
| Sulfur |
Sulfur of 0.025 % |
ISO 16120-4 Grade C10D2 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ISO 16120-4 Grade C10D2 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ISO 16120-4 Grade C10D2 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |