EN 10277-3 Grade 15SMn13 cold drawn
EN 10277-3 Grade 15SMn13 cold drawn introduction
The free cutting case hardening steel 15SMn13 is applicated for turned part production. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: ISO 15SMn13, ASTM A107 Grade 1117, SAE 1117, UNS G11170, DIN 1.0725, DIN 15SMn13, AFNOR 15SMn13, BS 15SMn13, BS 210M15, AISI 1117, JIS SUM31, EN 1.0725, GB 15SMn13, GB 210M15, ASTM Grade 1117
EN 10277-3 Grade 15SMn13 cold drawn general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10277-3 Grade 15SMn13 cold drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10277-3 Grade 15SMn13 cold drawn chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 - 0.18 % |
| Manganese |
Manganese of 0.9 - 1.3 % |
| Phosphorus |
Phosphorus of 0.06 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.08 - 0.18 % |
EN 10277-3 Grade 15SMn13 cold drawn magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10277-3 Grade 15SMn13 cold drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10277-3 Grade 15SMn13 cold drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 6 - 10 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 440 - 840 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 265 - 450 MPa |
- |