DIN 1651 Grade 15S10 cold drawn

DIN 1651 Grade 15S10 cold drawn

DIN 1651 Grade 15S10 cold drawn introduction

The fully killed machining steel 15 S 10 is applicated in the case hardened condition for thin walled parts with higher toughness demands.
Application: automotive engineering, toolbuilding, apparatus engineering

Equivalent material: DIN 1.0710, AFNOR 15S10, BS 15S10, AISI 1117, SAE 1117, EN 1.0710, ASTM 1117, UNS G11170

DIN 1651 Grade 15S10 cold drawn general

Property Temperature Value
Density 20.0 °C Density of 7.85 g/cm³

DIN 1651 Grade 15S10 cold drawn thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.08E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.19E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.1E-5 - 1.25E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.18E-5 - 1.3E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.36E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.32E-5 - 1.41E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.45E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.49E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 460 - 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 - 480 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 - 520 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 - 600 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 52.4 - 57.5 W/(m·K) -
- 100.0 °C Thermal conductivity of 55.7 W/(m·K) -
- 200.0 °C Thermal conductivity of 51.9 W/(m·K) -
- 300.0 °C Thermal conductivity of 47.6 W/(m·K) -
- 400.0 °C Thermal conductivity of 43.4 W/(m·K) -
- 500.0 °C Thermal conductivity of 39.6 W/(m·K) -
- 600.0 °C Thermal conductivity of 36 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 15.9 mm²/s -
- 100.0 °C Thermal diffusivity of 14.3 mm²/s -
- 200.0 °C Thermal diffusivity of 12.5 mm²/s -
- 300.0 °C Thermal diffusivity of 10.8 mm²/s -
- 400.0 °C Thermal diffusivity of 9.2 mm²/s -
- 500.0 °C Thermal diffusivity of 7.6 mm²/s -
- 600.0 °C Thermal diffusivity of 6.1 mm²/s -

DIN 1651 Grade 15S10 cold drawn chemical

Property Value
Carbon Carbon of 0.12 - 0.18 %
Manganese Manganese of 0.7 - 1.1 %
Phosphorus Phosphorus of 0.06 %
Silicon Silicon of 0.1 - 0.3 %
Sulfur Sulfur of 0.08 - 0.13 %

DIN 1651 Grade 15S10 cold drawn magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

DIN 1651 Grade 15S10 cold drawn electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 1.1E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.3E-7 Ω·m
- 200.0 °C Electrical resistivity of 3.04E-7 Ω·m
- 300.0 °C Electrical resistivity of 3.94E-7 Ω·m
- 400.0 °C Electrical resistivity of 5.01E-7 Ω·m
- 500.0 °C Electrical resistivity of 6.25E-7 Ω·m
- 600.0 °C Electrical resistivity of 7.7E-7 Ω·m

DIN 1651 Grade 15S10 cold drawn mechanical

Property Temperature Value
Elastic modulus -100.0 °C Elastic modulus of 217 GPa
- 20.0 °C Elastic modulus of 210 - 212 GPa
- 100.0 °C Elastic modulus of 207 GPa
- 200.0 °C Elastic modulus of 193 - 199 GPa
- 300.0 °C Elastic modulus of 185 - 192 GPa
- 400.0 °C Elastic modulus of 175 - 184 GPa
- 500.0 °C Elastic modulus of 175 GPa
- 600.0 °C Elastic modulus of 164 GPa
Elongation 20.0 °C Elongation of 6 - 10 %
Poisson's ratio 20.0 °C Poisson's ratio of 0.28 [-]
Shear modulus 20.0 °C Shear modulus of 81 GPa
Tensile strength 20.0 °C Tensile strength of 380 - 820 MPa
Yield strength 20.0 °C Yield strength of 250 - 420 MPa