ASTM A311 Grade 1117 Normal Draft Cold Drawn and Stress Relief Annealed
Equivalent material: DIN 1.0725, DIN 15SMn13, AFNOR 15SMn13, BS 15SMn13, BS 210M15, AISI 1117, SAE 1117, JIS SUM31, EN 15SMn13, EN 1.0725, ISO 15SMn13, GB 15SMn13, GB 210M15, UNS G11170
ASTM A311 Grade 1117 Normal Draft Cold Drawn and Stress Relief Annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A311 Grade 1117 Normal Draft Cold Drawn and Stress Relief Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A311 Grade 1117 Normal Draft Cold Drawn and Stress Relief Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 - 0.2 % |
| Manganese |
Manganese of 1 - 1.3 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.08 - 0.13 % |
ASTM A311 Grade 1117 Normal Draft Cold Drawn and Stress Relief Annealed magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A311 Grade 1117 Normal Draft Cold Drawn and Stress Relief Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A311 Grade 1117 Normal Draft Cold Drawn and Stress Relief Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 12 - 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 30 - 40 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 415 - 520 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 345 - 450 MPa |
- |