EN 10272 Grade X3CrNiMo17-13-3 solution annealed (+AT)
EN 10272 Grade X3CrNiMo17-13-3 solution annealed (+AT) introduction
The steel grade X3CrNiMo17-13-3 acc. to DIN EN 10272 : 2001-01is used for hot and cold formed rods for pressure vessels. The corrosion behaviour of the steel is similar to 1.4401. Slightly improved resistance to selective attack due to the higher Mo-content. The material is resistant to intercrystalline corrosion (ic) in delivery condition, in sensitized condition for cross sections up to 40 mm resistance to ic for cross sections up to 40 mm if the sensitization treatment of 10 min. has been carried out at 650°C +/- 10°C with subsequent cooling.
Equivalent material: AS 316, GB 0Cr17Ni12Mo2, CSN 17352, SFS 757, SFS X4CrNiMo17-12-3, AFNOR Z6CN17-12, BS 316S33, ISO 20a, UNI X5CrNiMo17-13, JIS SUS316, NS 14450, ÖNORM X5CrNiMo17-13-3KW, SS 2343, UNE F.3534, UNE X5CrNiMo17-12-2, ASTM 316, DIN X3CrNiMo17-13-3, GB 06Cr17Ni12Mo2, GB S31608, IS X04Cr17Ni12Mo2, KS STS316, AISI 316, ASME 316, SAE 316, UNS S31600, ISO X3CrNiMo17-12-3, ISO 4436-316-00-I, ISO AM32F, ASTM A479Type316, ASME SA-479Type316, AISI Type316, DIN X5CrNiMo17-13-3, DIN 1.4436, AFNOR Z7CND18-12-03, BS 316S13, UNI X8CrNiMo1713, SS 2347, JIS SUS316TKA, JIS SUS316TF, JIS SUS316FB, JIS SUSF316, JIS SUS316TKC, JIS SUS316TP, JIS SUS316TB, JIS SCS14, EN 1.4436, ISO A5
EN 10272 Grade X3CrNiMo17-13-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 - 8.01 g/cm³ |
EN 10272 Grade X3CrNiMo17-13-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.61E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.88E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.91E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.94E-5 1/K |
- |
| - |
900.0 °C |
Coefficient of thermal expansion of 1.97E-5 1/K |
- |
| - |
1000.0 °C |
Coefficient of thermal expansion of 2E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 440 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 472 - 500 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 487 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 503 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 512 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 541 J/(kg·K) |
- |
| - |
700.0 °C |
Specific heat capacity of 551 J/(kg·K) |
- |
| - |
800.0 °C |
Specific heat capacity of 559 J/(kg·K) |
- |
| - |
900.0 °C |
Specific heat capacity of 565 J/(kg·K) |
- |
| - |
1000.0 °C |
Specific heat capacity of 571 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 13.5 - 15 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 14.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 16.7 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 18.3 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 19.8 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 21.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 22.7 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 24.2 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 25.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 3.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 3.7 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.4 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.6 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.9 mm²/s |
- |
| - |
700.0 °C |
Thermal diffusivity of 5.2 mm²/s |
- |
| - |
800.0 °C |
Thermal diffusivity of 5.5 mm²/s |
- |
EN 10272 Grade X3CrNiMo17-13-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3 % |
| Nickel |
Nickel of 10.5 - 13 % |
| Nitrogen |
Nitrogen of 0.1 - 0.11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 - 0.03 % |
EN 10272 Grade X3CrNiMo17-13-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.5E-7 - 7.75E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 8.42E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 9.62E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.01E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.06E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.1E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.13E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.16E-6 Ω·m |
EN 10272 Grade X3CrNiMo17-13-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 206 GPa |
| - |
20.0 °C |
Elastic modulus of 196 - 200 GPa |
| - |
100.0 °C |
Elastic modulus of 190 - 194 GPa |
| - |
200.0 °C |
Elastic modulus of 182 - 186 GPa |
| - |
300.0 °C |
Elastic modulus of 174 - 179 GPa |
| - |
400.0 °C |
Elastic modulus of 166 - 172 GPa |
| - |
500.0 °C |
Elastic modulus of 158 - 165 GPa |
| - |
600.0 °C |
Elastic modulus of 150 GPa |
| - |
700.0 °C |
Elastic modulus of 142 GPa |
| - |
800.0 °C |
Elastic modulus of 134 GPa |
| Elongation |
20.0 °C |
Elongation of 40 % |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 30 % |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 215 [-] |
| Hardness, Brinell, trans |
20.0 °C |
Hardness, Brinell, trans of 215 [-] |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Shear modulus |
20.0 °C |
Shear modulus of 77.3 GPa |
| Tensile strength |
20.0 °C |
Tensile strength of 500 - 700 MPa |
| - |
100.0 °C |
Tensile strength of 460 MPa |
| - |
150.0 °C |
Tensile strength of 440 MPa |
| - |
200.0 °C |
Tensile strength of 420 MPa |
| - |
250.0 °C |
Tensile strength of 415 MPa |
| - |
300.0 °C |
Tensile strength of 410 MPa |
| - |
350.0 °C |
Tensile strength of 410 MPa |
| - |
400.0 °C |
Tensile strength of 410 MPa |
| - |
500.0 °C |
Tensile strength of 390 MPa |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 500 - 700 MPa |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 200 MPa |
| - |
100.0 °C |
Yield strength Rp0.2 of 175 MPa |
| - |
150.0 °C |
Yield strength Rp0.2 of 158 MPa |
| - |
200.0 °C |
Yield strength Rp0.2 of 145 MPa |
| - |
250.0 °C |
Yield strength Rp0.2 of 135 MPa |
| - |
300.0 °C |
Yield strength Rp0.2 of 127 MPa |
| - |
350.0 °C |
Yield strength Rp0.2 of 120 MPa |
| - |
400.0 °C |
Yield strength Rp0.2 of 115 MPa |
| - |
450.0 °C |
Yield strength Rp0.2 of 112 MPa |
| - |
500.0 °C |
Yield strength Rp0.2 of 110 MPa |
| - |
550.0 °C |
Yield strength Rp0.2 of 108 MPa |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 200 MPa |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 235 MPa |
| - |
100.0 °C |
Yield strength Rp1.0 of 210 MPa |
| - |
150.0 °C |
Yield strength Rp1.0 of 190 MPa |
| - |
200.0 °C |
Yield strength Rp1.0 of 175 MPa |
| - |
250.0 °C |
Yield strength Rp1.0 of 165 MPa |
| - |
300.0 °C |
Yield strength Rp1.0 of 155 MPa |
| - |
350.0 °C |
Yield strength Rp1.0 of 150 MPa |
| - |
400.0 °C |
Yield strength Rp1.0 of 145 MPa |
| - |
450.0 °C |
Yield strength Rp1.0 of 141 MPa |
| - |
500.0 °C |
Yield strength Rp1.0 of 139 MPa |
| - |
550.0 °C |
Yield strength Rp1.0 of 137 MPa |
| Yield strength Rp1.0, transverse |
20.0 °C |
Yield strength Rp1.0, transverse of 235 MPa |