EN 10217-7 Grade X3CrNiMo17-13-3 solution annealed (+AT)
EN 10217-7 Grade X3CrNiMo17-13-3 solution annealed (+AT) introduction
The austenitic steel X3CrNiMo17-13-3 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 300 °C) also in the welded condition.
Equivalent material: GB 06Cr17Ni12Mo2, GB S31608, JIS SUS316TB, JIS SUS316TF, KS STS316TB, AISI 316, ASTM A249Type316, ASTM A688Type316, AISI Type316, UNS S31600, DIN X5CrNiMo17-13-3, DIN 1.4436, DIN X3CrNiMo17-13-3, AFNOR Z7CND18-12-03, BS 316S13, UNI X8CrNiMo1713, SS 2343, SS 2347, SAE 316, JIS SUS316, JIS SUS316TKA, JIS SUS316FB, JIS SUSF316, JIS SUS316TKC, JIS SUS316TP, JIS SCS14, EN 1.4436, ISO A5
EN 10217-7 Grade X3CrNiMo17-13-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 - 8.01 g/cm³ |
EN 10217-7 Grade X3CrNiMo17-13-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.61E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.88E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.91E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.94E-5 1/K |
- |
| - |
900.0 °C |
Coefficient of thermal expansion of 1.97E-5 1/K |
- |
| - |
1000.0 °C |
Coefficient of thermal expansion of 2E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 440 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 472 - 500 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 487 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 503 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 512 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 541 J/(kg·K) |
- |
| - |
700.0 °C |
Specific heat capacity of 551 J/(kg·K) |
- |
| - |
800.0 °C |
Specific heat capacity of 559 J/(kg·K) |
- |
| - |
900.0 °C |
Specific heat capacity of 565 J/(kg·K) |
- |
| - |
1000.0 °C |
Specific heat capacity of 571 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 13.5 - 15 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 14.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 16.7 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 18.3 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 19.8 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 21.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 22.7 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 24.2 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 25.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 3.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 3.7 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.4 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.6 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.9 mm²/s |
- |
| - |
700.0 °C |
Thermal diffusivity of 5.2 mm²/s |
- |
| - |
800.0 °C |
Thermal diffusivity of 5.5 mm²/s |
- |
EN 10217-7 Grade X3CrNiMo17-13-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3 % |
| Nickel |
Nickel of 10.5 - 13 % |
| Nitrogen |
Nitrogen of 0.11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10217-7 Grade X3CrNiMo17-13-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.5E-7 - 7.75E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 8.42E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 9.62E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.01E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.06E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.1E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.13E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.16E-6 Ω·m |
EN 10217-7 Grade X3CrNiMo17-13-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 206 GPa |
| - |
20.0 °C |
Elastic modulus of 196 - 200 GPa |
| - |
100.0 °C |
Elastic modulus of 190 - 194 GPa |
| - |
200.0 °C |
Elastic modulus of 182 - 186 GPa |
| - |
300.0 °C |
Elastic modulus of 174 - 179 GPa |
| - |
400.0 °C |
Elastic modulus of 166 - 172 GPa |
| - |
500.0 °C |
Elastic modulus of 158 - 165 GPa |
| - |
600.0 °C |
Elastic modulus of 150 GPa |
| - |
700.0 °C |
Elastic modulus of 142 GPa |
| - |
800.0 °C |
Elastic modulus of 134 GPa |
| Elongation |
20.0 °C |
Elongation of 40 % |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 30 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Shear modulus |
20.0 °C |
Shear modulus of 77.3 GPa |
| Tensile strength |
20.0 °C |
Tensile strength of 510 - 710 MPa |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 510 - 710 MPa |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 205 MPa |
| - |
50.0 °C |
Yield strength Rp0.2 of 195 MPa |
| - |
100.0 °C |
Yield strength Rp0.2 of 175 MPa |
| - |
150.0 °C |
Yield strength Rp0.2 of 158 MPa |
| - |
200.0 °C |
Yield strength Rp0.2 of 145 MPa |
| - |
250.0 °C |
Yield strength Rp0.2 of 135 MPa |
| - |
300.0 °C |
Yield strength Rp0.2 of 127 MPa |
| - |
350.0 °C |
Yield strength Rp0.2 of 120 MPa |
| - |
400.0 °C |
Yield strength Rp0.2 of 115 MPa |
| - |
450.0 °C |
Yield strength Rp0.2 of 112 MPa |
| - |
500.0 °C |
Yield strength Rp0.2 of 110 MPa |
| - |
550.0 °C |
Yield strength Rp0.2 of 108 MPa |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 205 MPa |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 240 MPa |
| - |
50.0 °C |
Yield strength Rp1.0 of 228 MPa |
| - |
100.0 °C |
Yield strength Rp1.0 of 210 MPa |
| - |
150.0 °C |
Yield strength Rp1.0 of 190 MPa |
| - |
200.0 °C |
Yield strength Rp1.0 of 175 MPa |
| - |
250.0 °C |
Yield strength Rp1.0 of 165 MPa |
| - |
300.0 °C |
Yield strength Rp1.0 of 155 MPa |
| - |
350.0 °C |
Yield strength Rp1.0 of 150 MPa |
| - |
400.0 °C |
Yield strength Rp1.0 of 145 MPa |
| - |
450.0 °C |
Yield strength Rp1.0 of 141 MPa |
| - |
500.0 °C |
Yield strength Rp1.0 of 139 MPa |
| - |
550.0 °C |
Yield strength Rp1.0 of 137 MPa |