EN 10250-4 Grade X3CrNiMo17-13-3 solution annealed (+AT)
EN 10250-4 Grade X3CrNiMo17-13-3 solution annealed (+AT) introduction
The make X3CrNiMo17-13-3 is comparable to X5 CrNiMo 17 13 3 acc. to DIN17440 : 1985-07. Corrosion behaviour is similar to 1.4401. Slightly improved resistance to selective attack due to the higher Mo-content. In delivery condition resistant to intercrystalline corrosion. Application in chemical and pharmaceutical industry for acid resistant instruments, in cellulose, coloring, fatty acid, textile and rayon industry as well as in petrochemical industry.
Equivalent material: GB 06Cr17Ni12Mo2, GB S31608, IS X04Cr17Ni12Mo2, JIS SUSF316, JIS SUS316FB, KS STSF316, ASTM A473Type316, ASTM A965TypeF316, SAE 316, SAE Type316, SAE F316, SAE TypeF316, UNS S31600, DIN 1.4436, DIN X5CrNiMo17-13-3, DIN X3CrNiMo17-13-3, AFNOR Z7CND18-12-03, BS 316S13, UNI X8CrNiMo1713, SS 2343, SS 2347, AISI 316, JIS SUS316, JIS SUS316TKA, JIS SUS316TF, JIS SUS316TKC, JIS SUS316TP, JIS SUS316TB, JIS SCS14, EN 1.4436, ISO A5
EN 10250-4 Grade X3CrNiMo17-13-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 - 8.01 g/cm³ |
EN 10250-4 Grade X3CrNiMo17-13-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.61E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.88E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.91E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.94E-5 1/K |
- |
| - |
900.0 °C |
Coefficient of thermal expansion of 1.97E-5 1/K |
- |
| - |
1000.0 °C |
Coefficient of thermal expansion of 2E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 440 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 472 - 500 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 487 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 503 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 512 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 541 J/(kg·K) |
- |
| - |
700.0 °C |
Specific heat capacity of 551 J/(kg·K) |
- |
| - |
800.0 °C |
Specific heat capacity of 559 J/(kg·K) |
- |
| - |
900.0 °C |
Specific heat capacity of 565 J/(kg·K) |
- |
| - |
1000.0 °C |
Specific heat capacity of 571 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 13.5 - 15 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 14.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 16.7 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 18.3 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 19.8 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 21.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 22.7 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 24.2 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 25.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 3.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 3.7 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.4 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.6 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.9 mm²/s |
- |
| - |
700.0 °C |
Thermal diffusivity of 5.2 mm²/s |
- |
| - |
800.0 °C |
Thermal diffusivity of 5.5 mm²/s |
- |
EN 10250-4 Grade X3CrNiMo17-13-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3 % |
| Nickel |
Nickel of 10.5 - 13 % |
| Nitrogen |
Nitrogen of 0.11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
EN 10250-4 Grade X3CrNiMo17-13-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.75E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 8.42E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 9.62E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.01E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.06E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.1E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.13E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.16E-6 Ω·m |
EN 10250-4 Grade X3CrNiMo17-13-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 206 GPa |
| - |
20.0 °C |
Elastic modulus of 196 - 200 GPa |
| - |
100.0 °C |
Elastic modulus of 190 - 194 GPa |
| - |
200.0 °C |
Elastic modulus of 182 - 186 GPa |
| - |
300.0 °C |
Elastic modulus of 174 - 179 GPa |
| - |
400.0 °C |
Elastic modulus of 166 - 172 GPa |
| - |
500.0 °C |
Elastic modulus of 158 - 165 GPa |
| - |
600.0 °C |
Elastic modulus of 150 GPa |
| - |
700.0 °C |
Elastic modulus of 142 GPa |
| - |
800.0 °C |
Elastic modulus of 134 GPa |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 30 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Shear modulus |
20.0 °C |
Shear modulus of 77.3 GPa |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 500 - 700 MPa |
| Yield strength Rp0.2 |
100.0 °C |
Yield strength Rp0.2 of 177 MPa |
| - |
150.0 °C |
Yield strength Rp0.2 of 162 MPa |
| - |
200.0 °C |
Yield strength Rp0.2 of 147 MPa |
| - |
250.0 °C |
Yield strength Rp0.2 of 137 MPa |
| - |
300.0 °C |
Yield strength Rp0.2 of 127 MPa |
| - |
350.0 °C |
Yield strength Rp0.2 of 120 MPa |
| - |
400.0 °C |
Yield strength Rp0.2 of 115 MPa |
| - |
450.0 °C |
Yield strength Rp0.2 of 112 MPa |
| - |
500.0 °C |
Yield strength Rp0.2 of 110 MPa |
| - |
550.0 °C |
Yield strength Rp0.2 of 108 MPa |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 200 MPa |
| Yield strength Rp1.0 |
100.0 °C |
Yield strength Rp1.0 of 211 MPa |
| - |
150.0 °C |
Yield strength Rp1.0 of 191 MPa |
| - |
200.0 °C |
Yield strength Rp1.0 of 177 MPa |
| - |
250.0 °C |
Yield strength Rp1.0 of 167 MPa |
| - |
300.0 °C |
Yield strength Rp1.0 of 156 MPa |
| - |
350.0 °C |
Yield strength Rp1.0 of 150 MPa |
| - |
400.0 °C |
Yield strength Rp1.0 of 144 MPa |
| - |
450.0 °C |
Yield strength Rp1.0 of 141 MPa |
| - |
500.0 °C |
Yield strength Rp1.0 of 139 MPa |
| - |
550.0 °C |
Yield strength Rp1.0 of 137 MPa |
| Yield strength Rp1.0, transverse |
20.0 °C |
Yield strength Rp1.0, transverse of 235 MPa |