EN 10216-5 Grade X3CrNiMo17-13-3 solution annealed (+AT)
EN 10216-5 Grade X3CrNiMo17-13-3 solution annealed (+AT) introduction
X3CrNiMo17-13-3 is an austenitic steel that is resistant to intercrystalline corrosion. Temperature of solution is between 1020 and 1200°C (max. temperature is a reference data) and is cooled in water or air.
Equivalent material: GB 1Cr17Ni12Mo2, GB S31600, GB 0Cr17Ni12Mo2, GB S31608, JIS SUS316TB, JIS SUS316TF, KS STS316TB, AISI 316, SAE S31600, UNS S31600, ASME 316, ASTM 316, GB 06Cr17Ni12Mo2, AISI Type316, ASME SA-213Type316, ASTM A213Type316, DIN X5CrNiMo17-13-3, DIN 1.4436, DIN X3CrNiMo17-13-3, AFNOR Z7CND18-12-03, BS 316S13, UNI X8CrNiMo1713, SS 2343, SS 2347, SAE 316, JIS SUS316, JIS SUS316TKA, JIS SUS316FB, JIS SUSF316, JIS SUS316TKC, JIS SUS316TP, JIS SCS14, EN 1.4436, ISO A5
EN 10216-5 Grade X3CrNiMo17-13-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 g/cm³ |
EN 10216-5 Grade X3CrNiMo17-13-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10216-5 Grade X3CrNiMo17-13-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.05 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3 % |
| Nickel |
Nickel of 10.5 - 13 % |
| Nitrogen |
Nitrogen of 0.11 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10216-5 Grade X3CrNiMo17-13-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.5E-7 Ω·m |
EN 10216-5 Grade X3CrNiMo17-13-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 40 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 30 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 510 - 710 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 510 - 710 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |
| - |
50.0 °C |
Yield strength Rp0.2 of 195 MPa |
- |
| - |
100.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |
| - |
150.0 °C |
Yield strength Rp0.2 of 158 MPa |
- |
| - |
200.0 °C |
Yield strength Rp0.2 of 145 MPa |
- |
| - |
250.0 °C |
Yield strength Rp0.2 of 135 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 127 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 120 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 115 MPa |
- |
| - |
450.0 °C |
Yield strength Rp0.2 of 112 MPa |
- |
| - |
500.0 °C |
Yield strength Rp0.2 of 110 MPa |
- |
| - |
550.0 °C |
Yield strength Rp0.2 of 108 MPa |
- |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 205 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 240 MPa |
- |
| - |
50.0 °C |
Yield strength Rp1.0 of 228 MPa |
- |
| - |
100.0 °C |
Yield strength Rp1.0 of 210 MPa |
- |
| - |
150.0 °C |
Yield strength Rp1.0 of 190 MPa |
- |
| - |
200.0 °C |
Yield strength Rp1.0 of 175 MPa |
- |
| - |
250.0 °C |
Yield strength Rp1.0 of 165 MPa |
- |
| - |
300.0 °C |
Yield strength Rp1.0 of 155 MPa |
- |
| - |
350.0 °C |
Yield strength Rp1.0 of 150 MPa |
- |
| - |
400.0 °C |
Yield strength Rp1.0 of 145 MPa |
- |
| - |
450.0 °C |
Yield strength Rp1.0 of 141 MPa |
- |
| - |
500.0 °C |
Yield strength Rp1.0 of 139 MPa |
- |
| - |
550.0 °C |
Yield strength Rp1.0 of 137 MPa |
- |
| Yield strength Rp1.0, transverse |
20.0 °C |
Yield strength Rp1.0, transverse of 240 MPa |
- |