EN 10250-2 Grade C35 normalized and tempered (+NT)
EN 10250-2 Grade C35 normalized and tempered (+NT) introduction
Steel C35 is suitable for parts of slightly higher strength requirements and still low demands for ductility in vehicle, engine and machine engineering (e.g. gears, bolts, clutch parts).
Equivalent material: AS S1035, GB 35, GB U20352, IS 35C8, IS 3A, JIS S35C, GOST 35, ASTM A521 Grade 1035, SAE 1035, UNS G10350, DIN 1.0501, DIN C35, AFNOR C35, BS 060A35, UNI C35, SS 1550, UNE F.113, AISI 1034, SAE 1034, EN 1.0501, ISO C35, GB/T 35, GB/T U20352, UNS G10340
EN 10250-2 Grade C35 normalized and tempered (+NT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.82 g/cm³ |
EN 10250-2 Grade C35 normalized and tempered (+NT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 48 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 48.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 47.5 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.7 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 41.6 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 38.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.5 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 13.3 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 12.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 11.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.2 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.9 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.5 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
- |
EN 10250-2 Grade C35 normalized and tempered (+NT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.32 - 0.39 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10250-2 Grade C35 normalized and tempered (+NT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.17E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.62E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.32E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.2E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.23E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.41E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.8E-7 Ω·m |
EN 10250-2 Grade C35 normalized and tempered (+NT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 18 - 19 % |
- |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 14 - 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 470 - 520 MPa |
- |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 470 - 500 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 210 - 270 MPa |
- |
| Yield strength, transverse |
20.0 °C |
Yield strength, transverse of 210 - 245 MPa |
- |