EN 10132-3 Grade C35E soft annealed or soft annealed and skin passed (+A or +A+LC)
EN 10132-3 Grade C35E soft annealed or soft annealed and skin passed (+A or +A+LC) introduction
Cold-rolled narrow strip made of the mild steel C35E will be delivered in thicknesses up to 6 mm for quenching and tempering in following conditions:
- soft annealed or soft annealed and little rerolled (+A or +LC),
- cold rolled (+CR).
The delivery condition annealed to globular carbides (+AC) can be agreed.
Equivalent material: GB 35, GB U20352, ISO CS35, JIS S35C, ASTM A684 Grade 1035, UNS G10350, DIN Ck35, DIN 1.1181, DIN C35E, AFNOR C35E, AFNOR XC38H2, AFNOR C35RR, AFNOR XC35, AFNOR 9160C021, AFNOR 9160/C23, AFNOR XC38, AFNOR XC32, AFNOR XC38H1, BS En5, BS 080M30, BS C35E, BS 080M36, BS CFS6, AISI 1035, AISI 1038H, AISI 1038, AISI C1034, SAE 1035, SAE 1038H, SAE 1038, SAE C1034, JIS S35CM, JIS CS35, EN 1.1181, ISO C35E, ISO C35E4, ISO CE35E4, ISO S38C, GOST 35, GB/T ZG35, GB/T C22750, GB/T ZG270-500, GB/T 35, GB/T U20352, UNS H10380, UNS G10380
EN 10132-3 Grade C35E soft annealed or soft annealed and skin passed (+A or +A+LC) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.82 - 7.85 g/cm³ |
EN 10132-3 Grade C35E soft annealed or soft annealed and skin passed (+A or +A+LC) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 - 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 - 610 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 48 - 50 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 48.9 - 51 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 47.5 - 48.2 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.7 - 45.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 41.6 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 38.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.5 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 13.3 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 12.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 11.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10.2 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.9 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.5 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
- |
EN 10132-3 Grade C35E soft annealed or soft annealed and skin passed (+A or +A+LC) chemical
| Property |
Value |
| Carbon |
Carbon of 0.32 - 0.39 % |
| Chromium |
Chromium of 0.4 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Molybdenum |
Molybdenum of 0.1 % |
| Nickel |
Nickel of 0.4 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10132-3 Grade C35E soft annealed or soft annealed and skin passed (+A or +A+LC) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.2E-7 - 2.17E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.62E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.32E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.2E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.23E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.41E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.8E-7 Ω·m |
EN 10132-3 Grade C35E soft annealed or soft annealed and skin passed (+A or +A+LC) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 19 % |
- |
| Hardness, Rockwell B |
20.0 °C |
Hardness, Rockwell B of 86 [-] |
- |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 170 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 540 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 430 MPa |
- |
Collaborate with us to explore innovative possibilities using our cutting-edge steel technologies.