EN 10222-5 Grade X6CrNi18-10 solution annealed (+AT)
EN 10222-5 Grade X6CrNi18-10 solution annealed (+AT) introduction
The unstabilized austenitic steel X6CrNi18-10 (1.4948) shows good high-temperature strength up to 650 °C. Application in reactor engineering (sodium cooling circuit at fast breeders) as well as in steam boiler construction and in chemical industry.
Equivalent material: GB 07Cr19Ni10, GB S30409, IS X04Cr19Ni9, JIS SUSF304H, GOST 08Ch18N10, KS STSF304H, ASTM A182 Grade F304H, ASTM A965 Grade F304H, ASME SA-182 Grade F304H, UNS S30409, ISO X7CrNi18-9, GOST 08Х18Н10, DIN X6CrNi18-11, DIN 1.4948, DIN X6CrNi18-10, AFNOR Z6CN18-09, AISI 304H, SAE 304H, JIS SUS304H, JIS SUS304HTP, JIS SUS304HTB, JIS SUS304HTF, EN X6CrNi18-11, EN 1.4948, ASTM TP304H, ASTM S30409
EN 10222-5 Grade X6CrNi18-10 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.9 - 7.93 g/cm³ |
EN 10222-5 Grade X6CrNi18-10 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.61E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.67E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.72E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.77E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.81E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.84E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.88E-5 1/K | - |
| - | 700.0 °C | Coefficient of thermal expansion of 1.91E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.94E-5 1/K | - |
| - | 900.0 °C | Coefficient of thermal expansion of 1.97E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 2E-5 1/K | - |
| Max service temperature, long | - | Max service temperature, long of 0 - 750 °C | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 440 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 450 - 472 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 487 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 503 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 512 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 520 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 530 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 541 J/(kg·K) | - |
| - | 700.0 °C | Specific heat capacity of 551 J/(kg·K) | - |
| - | 800.0 °C | Specific heat capacity of 559 J/(kg·K) | - |
| - | 900.0 °C | Specific heat capacity of 565 J/(kg·K) | - |
| - | 1000.0 °C | Specific heat capacity of 571 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 14.3 - 17 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 15.8 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 17.5 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 19 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 20.5 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 21.9 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 23.3 W/(m·K) | - |
| - | 700.0 °C | Thermal conductivity of 24.6 W/(m·K) | - |
| - | 800.0 °C | Thermal conductivity of 26 W/(m·K) | - |
| - | 900.0 °C | Thermal conductivity of 27.4 W/(m·K) | - |
| - | 1000.0 °C | Thermal conductivity of 28.8 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 3.8 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 4 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 4.2 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 4.6 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 4.8 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 4.9 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 5 mm²/s | - |
| - | 700.0 °C | Thermal diffusivity of 5.3 mm²/s | - |
| - | 800.0 °C | Thermal diffusivity of 5.6 mm²/s | - |
| - | 900.0 °C | Thermal diffusivity of 5.9 mm²/s | - |
| - | 1000.0 °C | Thermal diffusivity of 6 mm²/s | - |
EN 10222-5 Grade X6CrNi18-10 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.04 - 0.08 % |
| Chromium | Chromium of 17 - 19 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 8 - 11 % |
| Nitrogen | Nitrogen of 0.1 - 0.11 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.015 % |
EN 10222-5 Grade X6CrNi18-10 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.1E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 7.76E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 8.49E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 9.14E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 9.71E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 1.02E-6 Ω·m |
| - | 600.0 °C | Electrical resistivity of 1.07E-6 Ω·m |
| - | 700.0 °C | Electrical resistivity of 1.1E-6 Ω·m |
| - | 800.0 °C | Electrical resistivity of 1.14E-6 Ω·m |
| - | 900.0 °C | Electrical resistivity of 1.17E-6 Ω·m |
| - | 1000.0 °C | Electrical resistivity of 1.19E-6 Ω·m |
EN 10222-5 Grade X6CrNi18-10 solution annealed (+AT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 206 GPa | - |
| - | 20.0 °C | Elastic modulus of 196 - 200 GPa | - |
| - | 100.0 °C | Elastic modulus of 190 GPa | - |
| - | 200.0 °C | Elastic modulus of 182 GPa | - |
| - | 300.0 °C | Elastic modulus of 174 GPa | - |
| - | 400.0 °C | Elastic modulus of 166 GPa | - |
| - | 500.0 °C | Elastic modulus of 158 GPa | - |
| - | 600.0 °C | Elastic modulus of 150 GPa | - |
| - | 700.0 °C | Elastic modulus of 142 GPa | - |
| - | 800.0 °C | Elastic modulus of 134 GPa | - |
| - | 900.0 °C | Elastic modulus of 127 GPa | - |
| - | 1000.0 °C | Elastic modulus of 120 GPa | - |
| Elongation | 20.0 °C | Elongation of 35 - 45 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 20.0 °C | Tensile strength of 490 - 690 MPa | - |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 195 MPa | - |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 230 MPa | - |
Count on us as your trusted partner for all your steel needs, from sourcing to delivery.
-- Our promise
Similar or equivalent steel materials
- EN 10272 Grade X5CrNi18-10 solution annealed (+AT)
- EN 10028-7 Grade X6CrNi18-10 solution annealed (+AT)
- EN 10216-5 Grade X6CrNi18-11 solution annealed (+AT)
- EN 10216-5 Grade X6CrNi18-10 solution annealed (+AT)
- EN 10250-4 Grade X5CrNi18-10 solution annealed (+AT)
- DIN 17460 Grade X6CrNi18-11 solution annealed (+AT)
- EN 10269 Grade X6CrNi18-10 solution annealed (+AT)
- EN 10088-1 Grade X5CrNi18-10 strain-hardened (+C700)
- ASTM A213 Grade TP304H Heat-Treated
- JIS G4307 Grade SUS304 cold-rolled, solution annealed
Get a quote