EN 10216-5 Grade X6CrNi18-10 solution annealed (+AT)
EN 10216-5 Grade X6CrNi18-10 solution annealed (+AT) introduction
The non-stabilised corrosion resistant austenitic steel X6CrNi18-10 (1.4948) is heat resistant up to 650 °C. Application mainly in the reactor engineering (Na-cooling circuits in fast breeders), in the steam boiler engineering as well as for pressure vessels and fastener parts. Acc. to DIN EN 1095 : 1999-05 it can be used as heat resistant steel.
Equivalent material: GB 07Cr19Ni10, GB S30409, UNS S30409, ASTM 304H, ASME 304H, ISO X7CrNi18-9, JIS SUS304HTB, JIS SUS304HTF, KS STS304HTB, ASTM A213Type304H, ASME SA-213Type304H, AISI 304H, AISI Type304H, DIN 1.4948, DIN X6CrNi18-11, DIN X6CrNi18-10, AFNOR Z6CN18-09, SAE 304H, JIS SUS304H, JIS SUS304HTP, JIS SUSF304H, EN X6CrNi18-11, EN 1.4948, ASTM TP304H, ASTM S30409
EN 10216-5 Grade X6CrNi18-10 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.9 - 7.93 g/cm³ |
EN 10216-5 Grade X6CrNi18-10 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.61E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.63E-5 - 1.67E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.69E-5 - 1.72E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.73E-5 - 1.77E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.78E-5 - 1.81E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.82E-5 - 1.84E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.85E-5 - 1.88E-5 1/K | - |
| - | 700.0 °C | Coefficient of thermal expansion of 1.87E-5 - 1.91E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.94E-5 1/K | - |
| - | 900.0 °C | Coefficient of thermal expansion of 1.97E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 2E-5 1/K | - |
| Max service temperature, long | - | Max service temperature, long of 0 - 750 °C | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 440 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 450 - 472 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 487 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 503 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 512 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 520 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 530 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 541 J/(kg·K) | - |
| - | 700.0 °C | Specific heat capacity of 551 J/(kg·K) | - |
| - | 800.0 °C | Specific heat capacity of 559 J/(kg·K) | - |
| - | 900.0 °C | Specific heat capacity of 565 J/(kg·K) | - |
| - | 1000.0 °C | Specific heat capacity of 571 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 14.3 - 17 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 15.8 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 17.5 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 19 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 20.5 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 21.9 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 23.3 W/(m·K) | - |
| - | 700.0 °C | Thermal conductivity of 24.6 W/(m·K) | - |
| - | 800.0 °C | Thermal conductivity of 26 W/(m·K) | - |
| - | 900.0 °C | Thermal conductivity of 27.4 W/(m·K) | - |
| - | 1000.0 °C | Thermal conductivity of 28.8 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 3.8 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 4 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 4.2 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 4.6 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 4.8 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 4.9 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 5 mm²/s | - |
| - | 700.0 °C | Thermal diffusivity of 5.3 mm²/s | - |
| - | 800.0 °C | Thermal diffusivity of 5.6 mm²/s | - |
| - | 900.0 °C | Thermal diffusivity of 5.9 mm²/s | - |
| - | 1000.0 °C | Thermal diffusivity of 6 mm²/s | - |
EN 10216-5 Grade X6CrNi18-10 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.04 - 0.08 % |
| Chromium | Chromium of 17 - 19 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 8 - 11 % |
| Nitrogen | Nitrogen of 0.11 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.015 % |
EN 10216-5 Grade X6CrNi18-10 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.1E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 7.76E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 8.49E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 9.14E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 9.71E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 1.02E-6 Ω·m |
| - | 600.0 °C | Electrical resistivity of 1.07E-6 Ω·m |
| - | 700.0 °C | Electrical resistivity of 1.1E-6 Ω·m |
| - | 800.0 °C | Electrical resistivity of 1.14E-6 Ω·m |
| - | 900.0 °C | Electrical resistivity of 1.17E-6 Ω·m |
| - | 1000.0 °C | Electrical resistivity of 1.19E-6 Ω·m |
EN 10216-5 Grade X6CrNi18-10 solution annealed (+AT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 206 GPa | - |
| - | 20.0 °C | Elastic modulus of 196 - 200 GPa | - |
| - | 100.0 °C | Elastic modulus of 190 GPa | - |
| - | 200.0 °C | Elastic modulus of 182 - 185 GPa | - |
| - | 300.0 °C | Elastic modulus of 174 - 175 GPa | - |
| - | 400.0 °C | Elastic modulus of 166 - 170 GPa | - |
| - | 500.0 °C | Elastic modulus of 158 - 160 GPa | - |
| - | 600.0 °C | Elastic modulus of 150 - 155 GPa | - |
| - | 700.0 °C | Elastic modulus of 142 - 145 GPa | - |
| - | 800.0 °C | Elastic modulus of 134 - 140 GPa | - |
| - | 900.0 °C | Elastic modulus of 127 - 135 GPa | - |
| - | 1000.0 °C | Elastic modulus of 120 - 125 GPa | - |
| Elongation | 20.0 °C | Elongation of 40 % | - |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 30 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 185 MPa | - |
| - | 50.0 °C | Yield strength Rp0.2 of 174 MPa | - |
| - | 100.0 °C | Yield strength Rp0.2 of 157 MPa | - |
| - | 150.0 °C | Yield strength Rp0.2 of 142 MPa | - |
| - | 200.0 °C | Yield strength Rp0.2 of 127 MPa | - |
| - | 250.0 °C | Yield strength Rp0.2 of 117 MPa | - |
| - | 300.0 °C | Yield strength Rp0.2 of 108 MPa | - |
| - | 350.0 °C | Yield strength Rp0.2 of 103 MPa | - |
| - | 400.0 °C | Yield strength Rp0.2 of 98 MPa | - |
| - | 450.0 °C | Yield strength Rp0.2 of 93 MPa | - |
| - | 500.0 °C | Yield strength Rp0.2 of 88 MPa | - |
| - | 550.0 °C | Yield strength Rp0.2 of 83 MPa | - |
| Yield strength Rp0.2, transverse | 20.0 °C | Yield strength Rp0.2, transverse of 185 MPa | - |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 225 MPa | - |
| - | 50.0 °C | Yield strength Rp1.0 of 201 MPa | - |
| - | 100.0 °C | Yield strength Rp1.0 of 191 MPa | - |
| - | 150.0 °C | Yield strength Rp1.0 of 172 MPa | - |
| - | 200.0 °C | Yield strength Rp1.0 of 157 MPa | - |
| - | 250.0 °C | Yield strength Rp1.0 of 147 MPa | - |
| - | 300.0 °C | Yield strength Rp1.0 of 137 MPa | - |
| - | 350.0 °C | Yield strength Rp1.0 of 132 MPa | - |
| - | 400.0 °C | Yield strength Rp1.0 of 127 MPa | - |
| - | 450.0 °C | Yield strength Rp1.0 of 122 MPa | - |
| - | 500.0 °C | Yield strength Rp1.0 of 118 MPa | - |
| - | 550.0 °C | Yield strength Rp1.0 of 113 MPa | - |
| Yield strength Rp1.0, transverse | 20.0 °C | Yield strength Rp1.0, transverse of 225 MPa | - |
Our state-of-the-art manufacturing ensures precision and impeccable finishes.
-- Our promise
Similar or equivalent steel materials
- Sandvik 5R10
- EN 10028-7 Grade X6CrNi18-10 solution annealed (+AT)
- EN 10216-5 Grade X6CrNi18-11 solution annealed (+AT)
- EN 10217-7 Grade X5CrNi18-10 solution annealed (+AT)
- EN 10222-5 Grade X6CrNi18-10 solution annealed (+AT)
- DIN 17460 Grade X6CrNi18-11 solution annealed (+AT)
- EN 10269 Grade X6CrNi18-10 solution annealed (+AT)
- ASTM A213 Grade TP304H Heat-Treated
- ASTM A249 Grade TP304H Heat-Treated
- ASTM A240 Grade 304H Heat-Treated