JIS G4307 Grade SUS304 cold-rolled, solution annealed
Equivalent material: GB/T 0Cr18Ni9, GB/T ML0Cr18Ni9, GB/T 0Cr18Ni9-R, GB/T 0Cr18Ni9-Q, GB/T 0Cr18Ni9-L, GB 0Cr18Ni9, GB 0Cr19Ni9N, GB 0Cr19Ni9, GB 1Cr19Ni9, GOST 08Х18Н10, GOST 08H18N10, AS 304, DIN X5CrNi1810, EN X5CrNi18-10, NF Z6CN18-09, NF Z5CN17-08, NF Z7CN18-09, NF Z4CN19-10FF, BS 304S31, BS 304S17, BS 304S25, BS 304S15, BS LW21, BS 304S16, UNI X5CrNi1810, UNI X5CrNi1810KG, UNI X5CrNi1810KW, UNI X5CrNi1810KT, ÖNORM X5CrNi1810S, ÖNORM X5CrNi1810KKW, UNE X5CrNi1810, SIS 2332, SIS 2333, MIL 304, MIL 304L, NF Z5CN18-09, BS S304S15, BS 304S59, IS 04Cr18Ni10, IS O4Cr18Ni10, UNE X6CrNi19-10, AMS 5501, AMS 5513, AMS 5560, AMS 5563, AMS 5564, AMS 5565, AMS 5566, AMS 5567, AMS 5639, AMS 5697, AMS 7228, AMS 7245, ASME 304, ASTM TP304, ASTM 304, ASTM B8, ASTM B8A, ASTM CR304, ASTM WP304, ASTM 18Cr 8Ni, ASTM F304, ASTM 8, ASTM FP304, ASTM MT304, ASTM 8A, MIL II, JIS SUS304TB, JIS SUS304TBS, JIS SUS304TKA, JIS SUS304TP, JIS SUSF304, AISI 304, SAE 304, JIS SUS304, ASTM S30400, ASTM Grade F304, UNS S30400, ASTM Grade 8, DIN 1.4301, DIN X 5 CrNi 18 9, DIN X5CrNi18-10, AFNOR Z6CN18-09, AFNOR Z7CN18-09, SS 2332, UNE F.3551, JIS SUS304TPD, JIS SUS304TPY, JIS SUS304TF, JIS SUS304TKC, EN 1.4301, ISO A2, GOST 08Ch18N10, ASTM Grade B8, ASTM Grade B8A
JIS G4307 Grade SUS304 cold-rolled, solution annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4307 Grade SUS304 cold-rolled, solution annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4307 Grade SUS304 cold-rolled, solution annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 18 - 20 % |
| Iron |
Iron of 66.35 - 74 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 8 - 10.5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
JIS G4307 Grade SUS304 cold-rolled, solution annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4307 Grade SUS304 cold-rolled, solution annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 40 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 206 MPa |
- |