EN 10222-5 Grade X5CrNiMo17-12-2 solution annealed (+AT)
EN 10222-5 Grade X5CrNiMo17-12-2 solution annealed (+AT) introduction
Trademark X5CrNiMo17-12-2 is an austenitic chrome-nickel-molybdenum-steel with increased resistance to non oxidizing acids and halogenated media, in delivery condition to intercrystalline corrosion. To the comparable material X 5 CrNiMo 17 12 2 applies: The material is suitable for mirror finishing and cold formable. Application for acid-resistant apparatuses in chemical and pharmaceutical industry, cellulose, rubber, color, fatty acid, textile and viscose industry, petrochemistry, for medical and photographical goods, in sewage plants, at higher chloride contents. Applicable in pressure vessel construction up to 300 °C., above that subject to authorization. It is applicated in construction trade for components with highest corrosion loadings (e.g. masonry anchorages in concrete, smokestacks, sanitary engineering, facades outside, lifts).
The Mo-alloyed rust-resistant steel is approved for load-bearing components.
Equivalent material: GB 06Cr17Ni12Mo2, GB S31608, IS X04Cr17Ni12Mo2, JIS SUSF316, KS STSF316, ASTM A965 Grade F316, UNS S31600, ASTM Grade F316, ASTM F316, DIN X5CrNiMo18-10, DIN 1.4401, DIN 316S42, DIN 316S33, DIN X5CrNiMo17-12-2, DIN X 5 CrNiMo 18 10, AFNOR Z7CND17-11-02, BS 316S16, UNI X5CrNiMo1712, SS 2347, UNE F.3543, AISI 316, SAE 316, JIS SUS316, JIS SUS316TKA, JIS SUS316TF, JIS SUS316FB, JIS SUS316TKC, JIS SUS316TP, JIS SUS316TB, JIS SUS316TBS, JIS SUS316TPY, JIS SUS316TPD, JIS SUS316HTP, JIS SUS316HTB, JIS SUS316HTF, JIS SUS316F, EN 1.4401, ISO A4, GOST 0Cr17Ni12Mo2, GB 08Ch27N13M2, ASTM 316
EN 10222-5 Grade X5CrNiMo17-12-2 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.96 - 8 g/cm³ |
| - |
22.0 °C |
Density of 7.96 g/cm³ |
EN 10222-5 Grade X5CrNiMo17-12-2 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.61E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.88E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.91E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.94E-5 1/K |
- |
| - |
900.0 °C |
Coefficient of thermal expansion of 1.97E-5 1/K |
- |
| - |
1000.0 °C |
Coefficient of thermal expansion of 2E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of 0 - 300 °C |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 440 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 472 - 500 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 487 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 503 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 512 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 541 J/(kg·K) |
- |
| - |
700.0 °C |
Specific heat capacity of 551 J/(kg·K) |
- |
| - |
800.0 °C |
Specific heat capacity of 559 J/(kg·K) |
- |
| - |
900.0 °C |
Specific heat capacity of 565 J/(kg·K) |
- |
| - |
1000.0 °C |
Specific heat capacity of 571 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 13.3 - 15 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 14.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 16.5 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 18.1 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 19.5 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 21 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 22.4 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 23.8 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 25.2 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 3.5 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 3.8 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.3 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.5 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.8 mm²/s |
- |
| - |
700.0 °C |
Thermal diffusivity of 5.1 mm²/s |
- |
| - |
800.0 °C |
Thermal diffusivity of 5.4 mm²/s |
- |
EN 10222-5 Grade X5CrNiMo17-12-2 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2 - 2.5 % |
| Nickel |
Nickel of 10 - 13 % |
| Nitrogen |
Nitrogen of 0.1 - 0.11 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10222-5 Grade X5CrNiMo17-12-2 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.91E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 8.45E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.19E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 9.77E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.03E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.08E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.12E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.15E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.18E-6 Ω·m |
EN 10222-5 Grade X5CrNiMo17-12-2 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 206 GPa |
| - |
20.0 °C |
Elastic modulus of 196 - 200 GPa |
| - |
22.0 °C |
Elastic modulus of 196.2 GPa |
| - |
24.0 °C |
Elastic modulus of 193.1 - 197.9 GPa |
| - |
100.0 °C |
Elastic modulus of 190 - 194 GPa |
| - |
149.0 °C |
Elastic modulus of 184.8 - 190.3 GPa |
| - |
200.0 °C |
Elastic modulus of 182 - 186 GPa |
| - |
260.0 °C |
Elastic modulus of 182 - 182.7 GPa |
| - |
300.0 °C |
Elastic modulus of 174 - 179 GPa |
| - |
371.0 °C |
Elastic modulus of 174.4 - 179.3 GPa |
| - |
400.0 °C |
Elastic modulus of 166 - 172 GPa |
| - |
483.0 °C |
Elastic modulus of 163.4 - 165.5 GPa |
| - |
500.0 °C |
Elastic modulus of 158 - 165 GPa |
| - |
593.0 °C |
Elastic modulus of 153.4 - 157.9 GPa |
| - |
600.0 °C |
Elastic modulus of 150 GPa |
| - |
700.0 °C |
Elastic modulus of 142 GPa |
| - |
704.0 °C |
Elastic modulus of 143.4 - 146.2 GPa |
| - |
800.0 °C |
Elastic modulus of 134 GPa |
| - |
816.0 °C |
Elastic modulus of 124.1 - 133.1 GPa |
| - |
900.0 °C |
Elastic modulus of 127 GPa |
| - |
1000.0 °C |
Elastic modulus of 120 GPa |
| Elongation |
20.0 °C |
Elongation of 35 - 45 % |
| Poisson's ratio |
22.0 °C |
Poisson's ratio of 0.29 [-] |
| - |
24.0 °C |
Poisson's ratio of 0.23 - 0.28 [-] |
| - |
149.0 °C |
Poisson's ratio of 0.24 - 0.28 [-] |
| - |
260.0 °C |
Poisson's ratio of 0.28 - 0.31 [-] |
| - |
371.0 °C |
Poisson's ratio of 0.33 - 0.36 [-] |
| - |
483.0 °C |
Poisson's ratio of 0.29 - 0.32 [-] |
| - |
593.0 °C |
Poisson's ratio of 0.32 [-] |
| - |
704.0 °C |
Poisson's ratio of 0.28 - 0.34 [-] |
| - |
816.0 °C |
Poisson's ratio of 0.22 - 0.27 [-] |
| Shear modulus |
22.0 °C |
Shear modulus of 75.8 GPa |
| - |
24.0 °C |
Shear modulus of 77.2 - 78.6 GPa |
| - |
149.0 °C |
Shear modulus of 74.5 GPa |
| - |
260.0 °C |
Shear modulus of 69.6 - 71 GPa |
| - |
371.0 °C |
Shear modulus of 64.1 - 67.6 GPa |
| - |
483.0 °C |
Shear modulus of 62.1 - 64.1 GPa |
| - |
593.0 °C |
Shear modulus of 57.9 - 60 GPa |
| - |
704.0 °C |
Shear modulus of 54.5 - 55.9 GPa |
| - |
816.0 °C |
Shear modulus of 51 - 52.4 GPa |
| Tensile strength |
20.0 °C |
Tensile strength of 510 - 710 MPa |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 205 MPa |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 240 MPa |
Let our innovative steel solutions unleash your creativity and drive excellence in your industry.