EN 10217-7 Grade X2CrNiMoN17-13-5 solution annealed (+AT)
EN 10217-7 Grade X2CrNiMoN17-13-5 solution annealed (+AT) introduction
The austenitic steel X2CrNiMoN17-13-5 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 400 °C) also in the welded condition.
Equivalent material: ASTM A249UNSS31726, UNS S31726, DIN 1.4439, DIN G-X3CrNiMoN17-13-5, DIN X2CrNiMoN17-13-5, AFNOR Z3CND18-14-05Az, UNE F.3544, AISI 317LMN, SAE 317LMN, JIS SUS317J1, EN 1.4439, ASTM 317LMN, ASTM Grade F48
EN 10217-7 Grade X2CrNiMoN17-13-5 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 8 - 8.01 g/cm³ |
EN 10217-7 Grade X2CrNiMoN17-13-5 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.61E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.88E-5 1/K | - |
| - | 700.0 °C | Coefficient of thermal expansion of 1.91E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.94E-5 1/K | - |
| - | 900.0 °C | Coefficient of thermal expansion of 1.97E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 2E-5 1/K | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 440 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 472 - 500 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 487 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 503 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 512 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 520 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 530 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 541 J/(kg·K) | - |
| - | 700.0 °C | Specific heat capacity of 551 J/(kg·K) | - |
| - | 800.0 °C | Specific heat capacity of 559 J/(kg·K) | - |
| - | 900.0 °C | Specific heat capacity of 565 J/(kg·K) | - |
| - | 1000.0 °C | Specific heat capacity of 571 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 13.5 - 14 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 14.9 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 16.7 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 18.3 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 19.8 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 21.3 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 22.7 W/(m·K) | - |
| - | 700.0 °C | Thermal conductivity of 24.2 W/(m·K) | - |
| - | 800.0 °C | Thermal conductivity of 25.6 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 3.6 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 3.7 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 4 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 4.4 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 4.6 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 4.7 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 4.9 mm²/s | - |
| - | 700.0 °C | Thermal diffusivity of 5.2 mm²/s | - |
| - | 800.0 °C | Thermal diffusivity of 5.5 mm²/s | - |
EN 10217-7 Grade X2CrNiMoN17-13-5 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 16.5 - 18.5 % |
| Manganese | Manganese of 2 % |
| Molybdenum | Molybdenum of 4 - 5 % |
| Nickel | Nickel of 12.5 - 14.5 % |
| Nitrogen | Nitrogen of 0.12 - 0.22 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.015 % |
EN 10217-7 Grade X2CrNiMoN17-13-5 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.75E-7 - 8.5E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 8.42E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 9.04E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 9.62E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 1.01E-6 Ω·m |
| - | 500.0 °C | Electrical resistivity of 1.06E-6 Ω·m |
| - | 600.0 °C | Electrical resistivity of 1.1E-6 Ω·m |
| - | 700.0 °C | Electrical resistivity of 1.13E-6 Ω·m |
| - | 800.0 °C | Electrical resistivity of 1.16E-6 Ω·m |
EN 10217-7 Grade X2CrNiMoN17-13-5 solution annealed (+AT) mechanical
| Property | Temperature | Value |
|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 206 GPa |
| - | 20.0 °C | Elastic modulus of 196 - 200 GPa |
| - | 100.0 °C | Elastic modulus of 190 - 194 GPa |
| - | 200.0 °C | Elastic modulus of 182 - 186 GPa |
| - | 300.0 °C | Elastic modulus of 174 - 179 GPa |
| - | 400.0 °C | Elastic modulus of 166 - 172 GPa |
| - | 500.0 °C | Elastic modulus of 158 - 165 GPa |
| - | 600.0 °C | Elastic modulus of 150 GPa |
| - | 700.0 °C | Elastic modulus of 142 GPa |
| - | 800.0 °C | Elastic modulus of 134 GPa |
| Elongation | 20.0 °C | Elongation of 35 % |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 30 % |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.28 [-] |
| Shear modulus | 20.0 °C | Shear modulus of 77.3 GPa |
| Tensile strength | 20.0 °C | Tensile strength of 580 - 800 MPa |
| Tensile strength, transverse | 20.0 °C | Tensile strength, transverse of 580 - 800 MPa |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 285 MPa |
| - | 50.0 °C | Yield strength Rp0.2 of 260 MPa |
| - | 100.0 °C | Yield strength Rp0.2 of 225 MPa |
| - | 150.0 °C | Yield strength Rp0.2 of 200 MPa |
| - | 200.0 °C | Yield strength Rp0.2 of 185 MPa |
| - | 250.0 °C | Yield strength Rp0.2 of 175 MPa |
| - | 300.0 °C | Yield strength Rp0.2 of 165 MPa |
| - | 350.0 °C | Yield strength Rp0.2 of 155 MPa |
| - | 400.0 °C | Yield strength Rp0.2 of 150 MPa |
| Yield strength Rp0.2, transverse | 20.0 °C | Yield strength Rp0.2, transverse of 285 MPa |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 315 MPa |
| - | 50.0 °C | Yield strength Rp1.0 of 290 MPa |
| - | 100.0 °C | Yield strength Rp1.0 of 255 MPa |
| - | 150.0 °C | Yield strength Rp1.0 of 230 MPa |
| - | 200.0 °C | Yield strength Rp1.0 of 210 MPa |
| - | 250.0 °C | Yield strength Rp1.0 of 200 MPa |
| - | 300.0 °C | Yield strength Rp1.0 of 190 MPa |
| - | 350.0 °C | Yield strength Rp1.0 of 180 MPa |
| - | 400.0 °C | Yield strength Rp1.0 of 175 MPa |
Trust our high-quality steel to forge a brighter and stronger future for your projects.
-- Our promise
Similar or equivalent steel materials
- EN 10088-1 Grade X2CrNiMoN17-13-5 solution annealed (+AT)
- DIN 17440 Grade X2CrNiMoN17-13-5 solution heat-treated and quenched
- DIN 17440 Grade X2CrNiMoN17-13-5 quenched (+Q)
- EN 10272 Grade X2CrNiMoN17-13-5 solution annealed (+AT)
- EN 10028-7 Grade X2CrNiMoN17-13-5 solution annealed (+AT)
- EN 10216-5 Grade X2CrNiMoN17-13-5 solution annealed (+AT)
- ASTM A182 Grade F48 Solution-Annealed
- DIN 17445 Grade G-X3CrNiMoN17-13-5 quenched (+Q)
- JIS G4303 Grade SUS317J1 solution treated
- JIS G4304 Grade SUS317J1 solution treated
Get a quote