EN 10213-4 Grade GX5CrNi19-10 solution heat-treated and quenched
EN 10213-4 Grade GX5CrNi19-10 solution heat-treated and quenched introduction
Material GX5CrNi19-10 is eqivalent to trademark G-X 6 CrNi 18 9 acc. to DIN17445-84. The DIN-material is predominantly used for fittings and in machine engineering, e.g. for pumps, centrifuges, agitators as well as for parts in food, dairy, beverage and packaging industry. This material is weldable without preheating.
Equivalent material: BDS 0Ch18N10SL, GB ZG0Cr18Ni9, SFS 387, SFS G-X8CrNi19-9, BS 304C15, BS 304C15LT, JIS SCS13, JUS CL45701, STAS T6NiCr180, STAS T7NiCr180, MSZ AöX7CrNi18-9, DIN G-X6CrNi18-9, DIN 1.4308, DIN GX5CrNi19-10, AFNOR Z6CN18.10M, EN 1.4308, ASTM Grade CPF8C (Ta max)
EN 10213-4 Grade GX5CrNi19-10 solution heat-treated and quenched general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.88 g/cm³ |
EN 10213-4 Grade GX5CrNi19-10 solution heat-treated and quenched thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.68E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.79E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.86E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -196 - 550 °C |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| Thermal conductivity |
50.0 °C |
Thermal conductivity of 15.2 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 16.5 W/(m·K) |
- |
EN 10213-4 Grade GX5CrNi19-10 solution heat-treated and quenched chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 18 - 20 % |
| Manganese |
Manganese of 1.5 % |
| Nickel |
Nickel of 8 - 11 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1.5 % |
| Sulfur |
Sulfur of 0.03 % |
EN 10213-4 Grade GX5CrNi19-10 solution heat-treated and quenched electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
EN 10213-4 Grade GX5CrNi19-10 solution heat-treated and quenched mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 30 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 440 - 640 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 200 MPa |
- |
| - |
100.0 °C |
Yield strength Rp1.0 of 160 MPa |
- |
| - |
200.0 °C |
Yield strength Rp1.0 of 125 MPa |
- |
| - |
300.0 °C |
Yield strength Rp1.0 of 110 MPa |
- |