EN 10213-4 Grade GX2CrNi19-11 solution heat-treated and quenched
EN 10213-4 Grade GX2CrNi19-11 solution heat-treated and quenched introduction
Material GX2CrNi19-11 belongs to the austenitic steel cast grades which are predominantly used for pressure vessels. This material is weldable without preheating and heat after treatment.
Equivalent material: DIN 1.4309, BS 304C12, AISI 304L, SAE 304L, JIS SCS13, EN 1.4309, ASTM CF3, ASTM Grade CPF3, UNS J92500
EN 10213-4 Grade GX2CrNi19-11 solution heat-treated and quenched general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.88 g/cm³ |
EN 10213-4 Grade GX2CrNi19-11 solution heat-treated and quenched thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.68E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.79E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.86E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| Thermal conductivity |
50.0 °C |
Thermal conductivity of 15.2 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 16.5 W/(m·K) |
- |
EN 10213-4 Grade GX2CrNi19-11 solution heat-treated and quenched chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 18 - 20 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 9 - 12 % |
| Nitrogen |
Nitrogen of 0.2 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1.5 % |
| Sulfur |
Sulfur of 0.025 % |
EN 10213-4 Grade GX2CrNi19-11 solution heat-treated and quenched electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
EN 10213-4 Grade GX2CrNi19-11 solution heat-treated and quenched mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 30 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 440 - 640 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 210 MPa |
- |
| - |
100.0 °C |
Yield strength Rp1.0 of 165 MPa |
- |
| - |
200.0 °C |
Yield strength Rp1.0 of 130 MPa |
- |
| - |
300.0 °C |
Yield strength Rp1.0 of 110 MPa |
- |
| - |
350.0 °C |
Yield strength Rp1.0 of 100 MPa |
- |
We are dedicated to helping you achieve success through our reliable steel solutions.
-- Our promise
Similar or equivalent steel materials