JIS G4304 Grade SUS304L solution treated
Equivalent material: GB/T 00Cr19Ni10, GB/T ZG00Cr18Ni10, GB/T 00Cr19Ni11-R, GB 00Cr19Ni10, GB 00Cr19Ni11, GOST 03Х18Н11, GOST 03H18N11, AS 304L, DIN X2CrNi1911, EN X2CrNi19-11, NF Z2CN18-10M, NF Z2CN18-10, NF Z3CN19-10M, NF Z3CN19-9M, NF Z3CND20-10M, NF Z2CND18-12M, NF Z1CN18-12, NF Z3CN18-10, NF Z3CN19-11, NF Z3CN19-11FF, BS 304S11, BS S.536, BS T.74, BS 304C12, BS 316C12, BS 304S22, BS LW20, BS LWCF20, BS LWCF21, UNI GX2CrNi1910, UNI X2CrNi1811, UNI X3CrNi1811, UNI X2CrNi1811KG, UNI X2CrNi1811KW, ÖNORM X2CrNi1911S, ÖNORM X2CrNi1911KKW, UNE AM-X2CrNiMo1911, UNE AM-X2CrNi1910, UNE X2CrNi1810, UNE F.310.G, SIS 2352, ASTM CF3, ASTM CF3A, ASTM CPF3, ASTM CPF3A, JIS SCS16A, JIS SCS19, JIS SCS19A, AS 304LL, NF Z2CN18-09, BS 304S12, IS 02Cr18Ni11, UNE X2CrNi1910, AMS 5511, AMS 5647, ASME 304L, ASTM TP304L, ASTM 304L, ASTM CR304L, ASTM WP304L, ASTM 18Cr 8Ni low C, ASTM F304L, ASTM MT304L, MIL 304L, JIS SUS304LTB, JIS SUS304LTBS, JIS SUS304LTP, JIS SUSF304L, AISI 304L, SAE 304L, DIN 1.4307, DIN G-X2CrNiN18-9, AFNOR Z3CN19-09, SS 2352, EN X2CrNi18-9, EN 1.4307, GOST 03Ch18N11, UNS S30403, IS X02Cr18Ni11, DIN 1.4650, AISI 304LCu, SAE 304LCu, EN X2CrNiCu19-10, EN 1.4650, ASTM S30403, DIN 1.4306, DIN X2CrNi19-11, DIN 19Cr11Ni, AFNOR Z3CN18-10, JIS SUS304LTPY, EN 1.4306, ISO A3, ASTM Grade CPF3
JIS G4304 Grade SUS304L solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS304L solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS304L solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS304L solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 480 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |
Rely on our strong, dependable steel to support your most critical applications.