DIN 17445 Grade G-X6CrNi18-9 quenched (+Q)
DIN 17445 Grade G-X6CrNi18-9 quenched (+Q) introduction
G-X 6 CrNi 18 9, forarmatures, pumps, centrifuges, mixers, parts for the food processing industry, dairy industry, beverages and packaging industry.
Equivalent material: ISO C47, ISO C47H, ISO C47L, DIN 1.4308, DIN GX5CrNi19-10, AFNOR Z6CN18.10M, BS 304C15, JIS SCS13, EN GX5CrNi19-10, EN 1.4308, ASTM Grade CPF8C (Ta max)
DIN 17445 Grade G-X6CrNi18-9 quenched (+Q) general
Property |
Temperature |
Value |
Density |
20.0 °C |
Density of 7.9 g/cm³ |
DIN 17445 Grade G-X6CrNi18-9 quenched (+Q) thermal
Property |
Temperature |
Value |
Comment |
Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
- |
200.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
- |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
- |
400.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
- |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
Max service temperature, long |
- |
Max service temperature, long of -196 - 550 °C |
- |
Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
DIN 17445 Grade G-X6CrNi18-9 quenched (+Q) chemical
Property |
Value |
Carbon |
Carbon of 0.07 % |
Chromium |
Chromium of 18 - 20 % |
Manganese |
Manganese of 1.5 % |
Nickel |
Nickel of 9 - 11 % |
Phosphorus |
Phosphorus of 0.05 % |
Silicon |
Silicon of 2 % |
Sulfur |
Sulfur of 0.03 % |
DIN 17445 Grade G-X6CrNi18-9 quenched (+Q) electrical
Property |
Temperature |
Value |
Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.3E-7 Ω·m |
DIN 17445 Grade G-X6CrNi18-9 quenched (+Q) mechanical
Property |
Temperature |
Value |
Comment |
Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
Elongation |
20.0 °C |
Elongation of 20 % |
- |
Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 130 - 200 [-] |
- |
Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
Tensile strength |
20.0 °C |
Tensile strength of 440 - 640 MPa |
- |
Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |
- |
100.0 °C |
Yield strength Rp0.2 of 145 MPa |
- |
- |
150.0 °C |
Yield strength Rp0.2 of 125 MPa |
- |
- |
200.0 °C |
Yield strength Rp0.2 of 119 MPa |
- |
- |
250.0 °C |
Yield strength Rp0.2 of 105 MPa |
- |
- |
300.0 °C |
Yield strength Rp0.2 of 100 MPa |
- |
Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 200 MPa |
- |
- |
100.0 °C |
Yield strength Rp1.0 of 170 MPa |
- |
- |
150.0 °C |
Yield strength Rp1.0 of 150 MPa |
- |
- |
200.0 °C |
Yield strength Rp1.0 of 140 MPa |
- |
- |
250.0 °C |
Yield strength Rp1.0 of 130 MPa |
- |
- |
300.0 °C |
Yield strength Rp1.0 of 125 MPa |
- |
Tailor-made steel solutions to meet your unique requirements.