EN 10139 Grade DC05 cold rolled, skin passed
EN 10139 Grade DC05 cold rolled, skin passed introduction
Cold rolled uncoated low carbon steel narrow strip for cold forming.,The non-alloy steel DC05 acc. to DIN EN 10130 is as special deep-draw quality suitable for cold forming of complexest profile forms, components and molded parts.To freedom of stretcher strains applies a period of 6 months after provision of the products for surface type A and B.
Welding:
DC05 is weldable by the following welding methods: MAG (metal-active-gas), plasma welding, laser welding, compression weld welding, resistance welding (spot, roll weld, buckle welding), arc welding.
The steel acts as substrate for surface refined and coated bands and sheets.
Application of DC05: car manufacturing, construction trade, traffic system.
Acc. to DIN EN 10139 DC05 is offered as cold rolled band or bar, cut in strength range HK270.
Equivalent material: ASTM A1008DDS, ASTM DDS, DIN 1.0312, DIN St 15, DIN DC05, AFNOR DC05, BS DC05, JIS SPCF, JIS SPCE, EN 1.0312, ISO CR4, ISO 04, ISO HR4
EN 10139 Grade DC05 cold rolled, skin passed general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10139 Grade DC05 cold rolled, skin passed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
EN 10139 Grade DC05 cold rolled, skin passed chemical
| Property |
Value |
| Carbon |
Carbon of 0.06 % |
| Manganese |
Manganese of 0.35 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Sulfur |
Sulfur of 0.025 % |
EN 10139 Grade DC05 cold rolled, skin passed electrical
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10139 Grade DC05 cold rolled, skin passed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation |
20.0 °C |
Elongation of 42 % |
- |
| Elongation A50 |
20.0 °C |
Elongation A50 of 34 - 42 % |
- |
| Elongation A80 |
20.0 °C |
Elongation A80 of 32 - 40 % |
- |
| Hardness, Vickers |
20.0 °C |
Hardness, Vickers of 100 - 110 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 270 - 330 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 140 - 220 MPa |
- |
Collaborate with us to explore innovative possibilities using our advanced steel technologies.