EN 10111 Grade DD12 hot rolled
EN 10111 Grade DD12 hot rolled introduction
The material meets deep drawing quality requirements.
Suitability for welding according to common methods.
The steel is suitable for application of surface coatings.
Equivalent material: AFNOR 2C, DIN RRStW23, IS SPHC, ASTM A1018CS1008, SAE 1008, UNS G10080, DIN 1.0398, EN 1.0398, DIN RStW 23, DIN DD12, AFNOR DD12, AISI 1008, BS HR3:DD12, JIS S PHC, JIS HR3, ISO HR3
EN 10111 Grade DD12 hot rolled general
| Property |
Value |
Comment |
| Density |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10111 Grade DD12 hot rolled thermal
| Property |
Value |
Comment |
| Coefficient of thermal expansion |
Coefficient of thermal expansion of 1.32e-05 - 1.38e-05 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
Max service temperature of 315.7 °C |
Predicted Value, Long |
| - |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10111 Grade DD12 hot rolled chemical
| Property |
Value |
Condition |
Related Standards |
Shape |
| Carbon |
Carbon of 0.1 % |
hot rolled |
EN 10111 |
Flat |
| Manganese |
Manganese of 0.45 % |
hot rolled |
EN 10111 |
Flat |
| Phosphorus |
Phosphorus of 0.035 % |
hot rolled |
EN 10111 |
Flat |
| Sulfur |
Sulfur of 0.035 % |
hot rolled |
EN 10111 |
Flat |
EN 10111 Grade DD12 hot rolled magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10111 Grade DD12 hot rolled electrical
| Property |
Value |
Comment |
| Electrical conductivity |
Electrical conductivity of 8 S/m |
Predicted Value |
| Electrical resistivity |
Electrical resistivity of 1.43e-07 - 1.74e-07 Ω·m |
Typical for Carbon Steel |
EN 10111 Grade DD12 hot rolled mechanical
| Property |
Value |
Comment |
| Elastic modulus |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Hardness, Brinell |
Hardness, Brinell of 272 [-] |
Predicted Value, Transverse |
| Poisson's ratio |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Reduction of area |
Reduction of area of 42.1 % |
Predicted Value |
| - |
Reduction of area of 44.0 % |
Predicted Value, Transverse |
| Shear modulus |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Shear strength |
Shear strength of 558 MPa |
Predicted Value |