EN 10028-2 Grade 20MnMoNi4-5 quenched and tempered (+QT)
EN 10028-2 Grade 20MnMoNi4-5 quenched and tempered (+QT) introduction
Alloy heat resistant and temperable high-grade steel for pressure vessel application at increased temperatures.
Application: turbine parts, high pressure tubes
Equivalent material: DIN 20MnMoNi4-5, IS SQV2A, IS SQV2B, ASTM A533 Grade B, ASTM A533 Grade C, ASTM A533 Grade D, UNS K12529, UNS K12539, UNS K12554, ASTM Grade B, ASTM K12539, IS 20MnMoNi4-5, DIN 1.6311, EN 1.6311, JIS SQV2B, JIS SFVQ1A, JIS SFVQ1B, JIS SQV2A, JIS SFVQ2B, ASTM Grade Type B
EN 10028-2 Grade 20MnMoNi4-5 quenched and tempered (+QT) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.84 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 20 °C | Density of 7.84 - 7.86 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 20 °C | Density of 7.86 g/cm³ | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat |
EN 10028-2 Grade 20MnMoNi4-5 quenched and tempered (+QT) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.05e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 20 °C | Coefficient of thermal expansion of 1.15e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 - 1.24e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 100 °C | Coefficient of thermal expansion of 1.24e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 - 1.29e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 200 °C | Coefficient of thermal expansion of 1.29e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 - 1.35e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 300 °C | Coefficient of thermal expansion of 1.35e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 - 1.39e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 400 °C | Coefficient of thermal expansion of 1.39e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 - 1.44e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 500 °C | Coefficient of thermal expansion of 1.44e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 1/K | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| Max service temperature | - | Max service temperature of 20 - 400 °C | quenched and tempered (+QT) | EN 10028-2 | Flat | Long |
| Melting point | - | Melting point of 1382 - 1529 °C | - | - | - | Typical for Nickel Molybdenum Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 20 °C | Specific heat capacity of 430 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 430 - 461 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 100 °C | Specific heat capacity of 479 - 500 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 100 °C | Specific heat capacity of 500 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 - 540 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 200 °C | Specific heat capacity of 540 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 - 580 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 300 °C | Specific heat capacity of 580 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 - 620 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 400 °C | Specific heat capacity of 620 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 558 - 690 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 500 °C | Specific heat capacity of 690 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 42 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Thermal conductivity of 42 - 44.3 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Thermal conductivity of 44.3 W/(m·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 100 °C | Thermal conductivity of 43 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 43 - 44 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 44 W/(m·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 200 °C | Thermal conductivity of 42.9 - 43 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 42.9 W/(m·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 200 °C | Thermal conductivity of 43 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 40.8 - 41 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 40.8 W/(m·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 300 °C | Thermal conductivity of 41 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 38.4 - 39 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 38.4 W/(m·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 400 °C | Thermal conductivity of 39 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 36 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 36 - 36.3 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 36.3 W/(m·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 600 °C | Thermal conductivity of 33.9 W/(m·K) | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 12.2 mm²/s | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 100 °C | Thermal diffusivity of 11.3 mm²/s | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 200 °C | Thermal diffusivity of 10.3 mm²/s | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 300 °C | Thermal diffusivity of 9.2 mm²/s | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 400 °C | Thermal diffusivity of 8.1 mm²/s | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 500 °C | Thermal diffusivity of 7 mm²/s | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 600 °C | Thermal diffusivity of 5.7 mm²/s | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
EN 10028-2 Grade 20MnMoNi4-5 quenched and tempered (+QT) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.01 - 0.05 % | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet |
| Carbon | Carbon of 0.15 - 0.23 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | Carbon of 0.23 % | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet |
| Chromium | Chromium of 0.2 % | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet |
| Copper | Copper of 0.2 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
| Manganese | Manganese of 1 - 1.5 % | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet |
| Molybdenum | Molybdenum of 0.4 - 0.6 % | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet |
| - | Molybdenum of 0.45 - 0.6 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
| Nickel | Nickel of 0.4 - 0.8 % | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet |
| Nitrogen | Nitrogen of 0.012 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | Nitrogen of 0.015 % | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet |
| Phosphorus | Phosphorus of 0.02 % | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet |
| Silicon | Silicon of 0.15 - 0.35 % | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet |
| - | Silicon of 0.4 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
| Sulfur | Sulfur of 0.01 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | Sulfur of 0.015 % | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet |
| Vanadium | Vanadium of 0.02 % | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet |
EN 10028-2 Grade 20MnMoNi4-5 quenched and tempered (+QT) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 7 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 2.35e-07 - 2.5e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.35e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 20 °C | Electrical resistivity of 2.5e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.91e-07 - 3e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 2.91e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 100 °C | Electrical resistivity of 3e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.68e-07 - 3.7e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.68e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 200 °C | Electrical resistivity of 3.7e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.6e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 400 °C | Electrical resistivity of 5.6e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.6e-07 - 5.66e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.66e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 500 °C | Electrical resistivity of 6.8e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.8e-07 - 6.81e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 6.81e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 600 °C | Electrical resistivity of 8.18e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
EN 10028-2 Grade 20MnMoNi4-5 quenched and tempered (+QT) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 20 °C | Elastic modulus of 211 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 211 - 212 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212 GPa | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 100 °C | Elastic modulus of 206 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 206 - 207 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207 GPa | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 200 °C | Elastic modulus of 199 GPa | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 300 °C | Elastic modulus of 191 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 191 - 192 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 192 GPa | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 400 °C | Elastic modulus of 183 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 183 - 184 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184 GPa | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 500 °C | Elastic modulus of 173 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 173 - 175 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 175 GPa | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| - | 600 °C | Elastic modulus of 164 GPa | quenched and tempered (+QT) | EN 10028-2, SEW 028 | Flat, Sheet | - |
| Elongation | - | Elongation of 15.0 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 16.0 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 16.4 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 18.0 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 20.6 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 18 % | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Elongation of 18 % | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| Hardness, Brinell | - | Hardness, Brinell of 251 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | - | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Nickel Molybdenum Steel |
| Reduction of area | - | Reduction of area of 42.9 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 43.6 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | - | Shear modulus of 80.9 GPa | - | - | - | Predicted Value |
| Shear strength | - | Shear strength of 617.4 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 560 - 750 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 560 - 730 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 560 - 710 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 560 - 700 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 560 - 750 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 560 - 730 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 560 - 710 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 560 - 700 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 570 - 750 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 570 - 730 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 570 - 710 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 570 - 700 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 570 - 750 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 570 - 730 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 570 - 710 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 570 - 700 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 590 - 750 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 590 - 730 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 590 - 710 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 590 - 700 MPa | quenched and tempered (+QT) | SEW 028, EN 10028-2 | Sheet, Flat | Transverse |
| - | 20 °C | Tensile strength of 590 - 750 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 590 - 730 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 590 - 710 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 590 - 700 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
Choose our top-tier steel products to elevate the quality and strength of your structures and equipment.
-- Our promise
Similar or equivalent steel materials
- EN 10028-2 Grade 15NiCuMoNb5-6-4 quenched and tempered (+QT)
- ASTM A542 Type A Class 1 Quenched and Tempered
- JIS G3472 Grade STAM390G
- JIS G3473 Grade STC440
- ASTM A420 Grade WPL6 Normalized, Normalized and Tempered, Annealed, or Quenched and Tempered
- DIWA 393 (EN 1.6311)
- JIS G3115 Grade SPV235
- JIS G3115 Grade SPV410
- JIS G3138 Grade SNR400B
- JIS G3138 Grade SNR490B