JIS G3115 Grade SPV235
Equivalent material: DIN 1.0345, DIN St 35.8, DIN ASt 35, DIN StE 255, DIN H I, DIN P235GH, AFNOR A37CP, AFNOR A37AP, BS 141-360, BS 161Gr.360, JIS SB410, JIS SGV410, JIS SPV24, JIS SPV410, JIS SPV450, JIS SPV490, EN P235GH, EN 1.0345, GOST 12k, GB 20, ASTM Grade B, ASTM Grade Ib, IS Grade1
JIS G3115 Grade SPV235 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3115 Grade SPV235 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3115 Grade SPV235 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3115 Grade SPV235 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3115 Grade SPV235 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 17 - 24 % |
- |
| Impact strength, Charpy notched |
0.0 °C |
Impact strength, Charpy notched of 27 kJ/m² |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 400 - 510 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 195 - 235 MPa |
- |
Experience the innovative edge of our steel solutions, designed to meet evolving industry needs.