EN 10028-2 Grade 15NiCuMoNb5-6-4 quenched and tempered (+QT)
EN 10028-2 Grade 15NiCuMoNb5-6-4 quenched and tempered (+QT) introduction
Alloy, heat resistant high-grade steel for pressure vessel application at increased temperatures.
Application: pressure vessel and steam boiler construction
Equivalent material: DIN 15NiCuMoNb5, EN 15NiCuMoNb5, IS SBV2, IS SBV3, ASTM A302 Grade C, ASTM A533 Grade B, ASTM A533 Grade C, ASTM A533 Grade D, UNS K12039, UNS K12529, UNS K12539, UNS K12554, IS 15NiCuMoNb5-6-4, BS 591, ASTM C, ASTM B, ASTM D, DIN 1.6368, EN 1.6368, DIN 15NiCuMoNb5-6-4, JIS SUS436LTP, JIS SUS436LTB, JIS SUS436L, JIS SUS436J1L, JIS SUS445J1, JIS SUSY308L, JIS SUSY347L, JIS SUS445J2
EN 10028-2 Grade 15NiCuMoNb5-6-4 quenched and tempered (+QT) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.85 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Sheet, Flat |
| - | 20 °C | Density of 7.85 - 7.851 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 20 °C | Density of 7.851 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 50 °C | Density of 7.842 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 100 °C | Density of 7.827 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 150 °C | Density of 7.811 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 200 °C | Density of 7.794 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 250 °C | Density of 7.777 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 300 °C | Density of 7.76 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 350 °C | Density of 7.742 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | 400 °C | Density of 7.724 g/cm³ | quenched and tempered (+QT) | EN 10028-2 | Flat |
EN 10028-2 Grade 15NiCuMoNb5-6-4 quenched and tempered (+QT) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.05e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 20 °C | Coefficient of thermal expansion of 1.15e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 - 1.22e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 100 °C | Coefficient of thermal expansion of 1.22e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 - 1.29e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 200 °C | Coefficient of thermal expansion of 1.29e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 - 1.34e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 300 °C | Coefficient of thermal expansion of 1.34e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 - 1.4e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 400 °C | Coefficient of thermal expansion of 1.4e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.43e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 600 °C | Coefficient of thermal expansion of 1.46e-05 1/K | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| Max service temperature | - | Max service temperature of -10 - 500 °C | quenched and tempered (+QT) | EN 10028-2 | Flat | Long |
| - | - | Max service temperature of 20 - 500 °C | quenched and tempered (+QT) | EN 10028-2 | Flat | Long |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 20 °C | Specific heat capacity of 430 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 430 - 461 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 100 °C | Specific heat capacity of 479 - 500 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 100 °C | Specific heat capacity of 500 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 - 540 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 200 °C | Specific heat capacity of 540 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 - 580 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 300 °C | Specific heat capacity of 580 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 - 620 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 400 °C | Specific heat capacity of 620 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 690 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 600 °C | Specific heat capacity of 780 J/(kg·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 38 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Thermal conductivity of 38 - 38.6 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Thermal conductivity of 38.6 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 100 °C | Thermal conductivity of 40.4 - 41 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 40.4 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 100 °C | Thermal conductivity of 41 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 41.3 - 42 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 41.3 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 200 °C | Thermal conductivity of 42 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 40.7 - 41 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 40.7 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 300 °C | Thermal conductivity of 41 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 39 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 39 - 39.3 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 39.3 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 500 °C | Thermal conductivity of 38 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal conductivity of 35 W/(m·K) | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 10.7 mm²/s | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 100 °C | Thermal diffusivity of 10.4 mm²/s | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 200 °C | Thermal diffusivity of 9.9 mm²/s | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 300 °C | Thermal diffusivity of 9.2 mm²/s | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 400 °C | Thermal diffusivity of 8.3 mm²/s | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
EN 10028-2 Grade 15NiCuMoNb5-6-4 quenched and tempered (+QT) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.015 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Carbon | Carbon of 0.17 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Chromium | Chromium of 0.3 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Copper | Copper of 0.5 - 0.8 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Manganese | Manganese of 0.8 - 1.2 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Molybdenum | Molybdenum of 0.25 - 0.5 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Nickel | Nickel of 1 - 1.3 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Niobium | Niobium of 0.015 - 0.045 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Nitrogen | Nitrogen of 0.02 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Phosphorus | Phosphorus of 0.03 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Silicon | Silicon of 0.25 - 0.5 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet |
| Sulfur | Sulfur of 0.01 % | quenched and tempered (+QT) | EN 10028-2 | Flat |
| - | Sulfur of 0.025 % | quenched and tempered (+QT) | EN 10028-2 | Sheet, Flat |
EN 10028-2 Grade 15NiCuMoNb5-6-4 quenched and tempered (+QT) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 5 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 2.7e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 50 °C | Electrical resistivity of 2.87e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 3.17e-07 - 3.2e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 3.17e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 100 °C | Electrical resistivity of 3.2e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 150 °C | Electrical resistivity of 3.49e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.8e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.8e-07 - 3.82e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 3.82e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 250 °C | Electrical resistivity of 4.21e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.6e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.6e-07 - 4.61e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.61e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 350 °C | Electrical resistivity of 5.06e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.5e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.5e-07 - 5.54e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.54e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 500 °C | Electrical resistivity of 6.6e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 7.8e-07 Ω·m | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
EN 10028-2 Grade 15NiCuMoNb5-6-4 quenched and tempered (+QT) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 20 °C | Elastic modulus of 208.4 - 211 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 208.4 - 212 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 208.4 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 211 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 211 - 212 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 50 °C | Elastic modulus of 206.9 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 204.1 - 206 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 204.1 - 207 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 204.1 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 206 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 206 - 207 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 150 °C | Elastic modulus of 200.6 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 196.9 - 200 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 196.9 - 199 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 196.9 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 199 - 200 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 199 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 200 °C | Elastic modulus of 200 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 250 °C | Elastic modulus of 193.2 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 189.2 - 192 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 189.2 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 192 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 350 °C | Elastic modulus of 185.2 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 181.0 - 184 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 181.0 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | - |
| - | 500 °C | Elastic modulus of 175 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 164 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| Elongation | - | Elongation of 15.5 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 15.7 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 16.6 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 19.4 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 20.8 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 16 % | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | Transverse |
| - | 20 °C | Elongation of 16 % | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| Hardness, Brinell | - | Hardness, Brinell of 253 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | 20 °C | Poisson's ratio of 0.289 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 50 °C | Poisson's ratio of 0.289 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Poisson's ratio of 0.291 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 150 °C | Poisson's ratio of 0.291 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Poisson's ratio of 0.292 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 250 °C | Poisson's ratio of 0.294 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Poisson's ratio of 0.295 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 350 °C | Poisson's ratio of 0.298 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Poisson's ratio of 0.305 [-] | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| Reduction of area | - | Reduction of area of 39.2 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 44.4 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | 20 °C | Shear modulus of 80.8 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 50 °C | Shear modulus of 80.2 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 100 °C | Shear modulus of 79.0 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 150 °C | Shear modulus of 77.7 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 200 °C | Shear modulus of 76.2 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 250 °C | Shear modulus of 74.7 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 300 °C | Shear modulus of 73.1 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 350 °C | Shear modulus of 71.3 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 400 °C | Shear modulus of 69.4 GPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| Shear strength | - | Shear strength of 637.1 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 580 - 740 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat, Sheet | Transverse |
| - | 20 °C | Tensile strength of 580 - 740 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 590 - 740 MPa | quenched and tempered (+QT) | EN 10028-2 | Flat | Transverse |
Unlock the potential of your projects and drive success with our high-performance steel.
-- Our promise
Similar or equivalent steel materials
- EN 10028-2 Grade 20MnMoNi4-5 quenched and tempered (+QT)
- EN 10088-1 Grade X2CrMoTi17-1 soft annealed (+A)
- DIWA 373 (EN 1.6368)
- JIS G4304 Grade SUS436L annealed
- JIS G4304 Grade SUS445J1 annealed
- JIS G4305 Grade SUS436L annealed
- JIS G4305 Grade SUS445J1 annealed
- JIS G3106 Grade SM520C
- JIS G3106 Grade SM490C
- JIS G3106 Grade SM520B
Get a quote