EN 10025-2 Grade S355J0 normalized or normalized formed (+N)
EN 10025-2 Grade S355J0 normalized or normalized formed (+N) introduction
The hot rolled, unalloyed quality steel S355J0 is a higher strength fine grained steel for dynamic loaded steel structural engineering. Dimensioning advantages in respect to the S235J2 due to the by 120 MPa higher yield strength. The steel shows a by 15% higher resistance to mineral wear due to sliding action in comparison to S235J2.
The steel is not intended for heat treatment. Stress relieving annealing is allowed. Products in the delivery condition +N may be hot formed and/or normalized after delivery.
For long products and continuous rolled flats the delivery condition is up to the producer +AR, +N or +M. The delivery condition of four-high rolled sheet is also up to the producer and may be +AR or +N. Both conditions can be ordered.
For this steel are available (mat. no 1.0554, S355J0C) grades for folding, roll forming to shape and cold drawing.
Equivalent material: IS Fe540, IS E350, IS S355C, ASTM A633 Grade C, ASTM A572 Grade 55, ASTM A1011 HSLAS Grade 55, UNS K12000, DIN St52-3U, DIN Fe510C, DIN 1.0553, EN Fe510C, EN 1.0553, DIN St 52-3 U, DIN S355J0, AFNOR S355J0, UNI Fe510C, AISI 345A, BS 50C, BS S355J0, SAE 345A, JIS E355C, ISO S355C, ISO Fe510C, GOST 17Г1С
EN 10025-2 Grade S355J0 normalized or normalized formed (+N) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.84 g/cm³ | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
EN 10025-2 Grade S355J0 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.08e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Coefficient of thermal expansion of 1.19e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Coefficient of thermal expansion of 1.25e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Coefficient of thermal expansion of 1.3e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Coefficient of thermal expansion of 1.41e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Coefficient of thermal expansion of 1.45e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Coefficient of thermal expansion of 1.49e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Max service temperature | - | Max service temperature of 368.8 °C | - | - | - | Predicted Value, Long |
| - | - | Max service temperature of 500 °C | - | - | - | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | - | - | - | Typical for Low Carbon Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 46.5 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Thermal conductivity of 47.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Thermal conductivity of 45.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Thermal conductivity of 43.5 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Thermal conductivity of 40.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Thermal conductivity of 38.1 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Thermal conductivity of 35.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 12.9 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Thermal diffusivity of 12.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Thermal diffusivity of 11.1 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Thermal diffusivity of 9.9 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Thermal diffusivity of 8.7 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Thermal diffusivity of 7.3 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Thermal diffusivity of 5.9 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
EN 10025-2 Grade S355J0 normalized or normalized formed (+N) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.2 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Copper | Copper of 0.55 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Manganese | Manganese of 1.6 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Nitrogen | Nitrogen of 0.012 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Phosphorus | Phosphorus of 0.03 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Silicon | Silicon of 0.55 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Sulfur | Sulfur of 0.03 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
EN 10025-2 Grade S355J0 normalized or normalized formed (+N) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10025-2 Grade S355J0 normalized or normalized formed (+N) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 7 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 2.24e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Electrical resistivity of 2.71e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Electrical resistivity of 3.44e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Electrical resistivity of 4.31e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Electrical resistivity of 5.32e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Electrical resistivity of 6.5e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Electrical resistivity of 7.86e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
EN 10025-2 Grade S355J0 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Elongation | - | Elongation of 17.6 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 19.6 % | - | - | - | Predicted Value, A50 |
| - | - | Elongation of 22.4 % | - | - | - | Predicted Value, A5 |
| - | 20 °C | Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 13 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 19 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 20 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 20 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 21 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 22 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Hardness, Brinell | - | Hardness, Brinell of 244 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | - | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Low Carbon Steel |
| Reduction of area | - | Reduction of area of 44.3 % | - | - | - | Predicted Value, Transverse |
| - | - | Reduction of area of 51.9 % | - | - | - | Predicted Value |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 508.4 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 450 - 680 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 450 - 630 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 450 - 600 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 470 - 680 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 470 - 630 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 470 - 600 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 510 - 680 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 510 - 630 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 510 - 600 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Yield strength | - | Yield strength of 243.8 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 309.1 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 368.5 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 383.4 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 400.2 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 475.2 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 480.2 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 275 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 285 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 295 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 315 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 325 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 335 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 345 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 355 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
Simplify your procurement process with our comprehensive range of steel products.
-- Our promise
Similar or equivalent steel materials
- EN 10025-2 Grade S355J2 normalized or normalized formed (+N)
- EN 10028-3 Grade P355N normalized or normalized formed (+N)
- DIN 5512-1 Grade S355J2G3 normalized or normalized formed (+N)
- DIN 1623-2 Grade S325G skin passed
- EN 10277-2 Grade St52-3 cold drawn
- EN 10277-2 Grade St52-3 cold drawn or turned and normalized
- EN 10277-2 Grade St52-3 turned
- DIN 2393-2 Grade St 52-3 normalized or normalized formed (+N)
- DIN 2393-2 Grade St 52-3 bright drawn and stress relieved
- EN 10305-3 Grade St 52-3 normalized or normalized formed (+N)
Get a quote