EN 10025-2 Grade S355J2 normalized or normalized formed (+N)

Home
Material
EN 10025-2 Grade S355J2 normalized or normalized formed (+N)

EN 10025-2 Grade S355J2 normalized or normalized formed (+N)

EN 10025-2 Grade S355J2 normalized or normalized formed (+N) introduction

EN S355J2 is a corrosion resistant, low alloy structural steel, that is known for its good forming properties and high durability. It offers high strength and can be welded to other weldable steels.

Equivalent material: IS E350, ASTM A1011 HSLAS Grade 55, DIN S355J2, EN S355J2G4, DIN Fe510D2, DIN St52-3, DIN 1.0570, EN 1.0570, DIN St 52-3, DIN St 52-3 G, DIN St 53-3 N, DIN S355J2G3, DIN S325G, FNOR S355J2G3, AFNOR E36-3, UNI Fe510B, AISI 345A, AISI 1024, BS 50 D, BS S355J2G3, SAE 345A, SAE 1024, JIS SKK490, JIS SM50, JIS SM53, JIS SM490, JIS SM520, JIS STK50, JIS STK51, JIS STK490, JIS STK500, JIS STKR50, JIS STKR490, JIS SM490A, JIS SM490B, JIS SM490C, JIS SM490YA, JIS SM490YB, JIS SM520B, JIS SM520C, JIS SKY490, ISO S355D, GOST 17G1S, GOST 17GS, GB/T 16MnDR, GB/T L20173, GB/T 16Mn, GB/T L20166, UNS K02003, UNS K03011, UNS K03014, UNS K12037, UNS K12709, IS Fe540W-HT, DIN 1.0577, EN 1.0577, DIN St 52-3 N, DIN S355J2G4, AFNOR S355J2, AFNOR A52FP, BS 50D, BS EN50D, BS S355J2, JIS SPHF, ASTM LF2, UNS K12447

EN 10025-2 Grade S355J2 normalized or normalized formed (+N) general

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20 °C	Density of 7.83 g/cm³	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire

EN 10025-2 Grade S355J2 normalized or normalized formed (+N) thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	-100 °C	Coefficient of thermal expansion of 1.08e-05 1/K	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Coefficient of thermal expansion of 1.19e-05 1/K	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	100 °C	Coefficient of thermal expansion of 1.25e-05 1/K	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	200 °C	Coefficient of thermal expansion of 1.3e-05 1/K	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	300 °C	Coefficient of thermal expansion of 1.36e-05 1/K	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	400 °C	Coefficient of thermal expansion of 1.41e-05 1/K	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	500 °C	Coefficient of thermal expansion of 1.45e-05 1/K	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	600 °C	Coefficient of thermal expansion of 1.49e-05 1/K	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
Max service temperature	-	Max service temperature of 305.4 °C	-	-	-	Predicted Value, Long
-	-	Max service temperature of 500 °C	-	-	-	Typical for Carbon Steel
Melting point	-	Melting point of 1480 - 1526 °C	-	-	-	Typical for Low Carbon Steel
Specific heat capacity	-100 °C	Specific heat capacity of 423 J/(kg·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Specific heat capacity of 461 J/(kg·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	100 °C	Specific heat capacity of 479 J/(kg·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	200 °C	Specific heat capacity of 499 J/(kg·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	300 °C	Specific heat capacity of 517 J/(kg·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	400 °C	Specific heat capacity of 536 J/(kg·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	500 °C	Specific heat capacity of 558 J/(kg·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	600 °C	Specific heat capacity of 587 J/(kg·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
Thermal conductivity	-100 °C	Thermal conductivity of 37.6 W/(m·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Thermal conductivity of 42.2 W/(m·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	100 °C	Thermal conductivity of 43.2 W/(m·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	200 °C	Thermal conductivity of 42.9 W/(m·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	300 °C	Thermal conductivity of 41.2 W/(m·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	400 °C	Thermal conductivity of 39.1 W/(m·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	500 °C	Thermal conductivity of 36.6 W/(m·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	600 °C	Thermal conductivity of 34.1 W/(m·K)	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
Thermal diffusivity	-100 °C	Thermal diffusivity of 12.9 mm²/s	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Thermal diffusivity of 11.7 mm²/s	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	100 °C	Thermal diffusivity of 11.2 mm²/s	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	200 °C	Thermal diffusivity of 10.3 mm²/s	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	300 °C	Thermal diffusivity of 9.4 mm²/s	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	400 °C	Thermal diffusivity of 8.3 mm²/s	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	500 °C	Thermal diffusivity of 7.1 mm²/s	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	600 °C	Thermal diffusivity of 5.7 mm²/s	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-

EN 10025-2 Grade S355J2 normalized or normalized formed (+N) chemical

Property	Value	Condition	Related Standards	Shape
Carbon	Carbon of 0.2 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire
Copper	Copper of 0.55 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire
Manganese	Manganese of 1.6 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire
Phosphorus	Phosphorus of 0.025 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire
Silicon	Silicon of 0.55 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire
Sulfur	Sulfur of 0.025 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire

EN 10025-2 Grade S355J2 normalized or normalized formed (+N) magnetic

Property	Value	Comment
Curie temperature	Curie temperature of 770 °C	Typical for Low Carbon Steel

EN 10025-2 Grade S355J2 normalized or normalized formed (+N) electrical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Electrical conductivity	-	Electrical conductivity of 7 S/m	-	-	-	Predicted Value
Electrical resistivity	-100 °C	Electrical resistivity of 1.82e-07 Ω·m	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Electrical resistivity of 2.47e-07 Ω·m	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	100 °C	Electrical resistivity of 2.96e-07 Ω·m	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	200 °C	Electrical resistivity of 3.68e-07 Ω·m	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	300 °C	Electrical resistivity of 4.55e-07 Ω·m	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	400 °C	Electrical resistivity of 5.56e-07 Ω·m	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	500 °C	Electrical resistivity of 6.75e-07 Ω·m	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	600 °C	Electrical resistivity of 8.13e-07 Ω·m	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-

EN 10025-2 Grade S355J2 normalized or normalized formed (+N) mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	-100 °C	Elastic modulus of 217 GPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Elastic modulus of 212 GPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	100 °C	Elastic modulus of 207 GPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	200 °C	Elastic modulus of 199 GPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	300 °C	Elastic modulus of 192 GPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	400 °C	Elastic modulus of 184 GPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	500 °C	Elastic modulus of 175 GPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	600 °C	Elastic modulus of 164 GPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
Elongation	-	Elongation of 17.7 %	-	-	-	Predicted Value, A200
-	-	Elongation of 19.6 %	-	-	-	Predicted Value, A50
-	-	Elongation of 22.3 %	-	-	-	Predicted Value, A5
-	20 °C	Elongation of 12 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80 Transverse
-	20 °C	Elongation of 13 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80 Transverse
-	20 °C	Elongation of 14 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80 Transverse
-	20 °C	Elongation of 14 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80
-	20 °C	Elongation of 15 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80 Transverse
-	20 °C	Elongation of 15 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80
-	20 °C	Elongation of 16 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80 Transverse
-	20 °C	Elongation of 16 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80
-	20 °C	Elongation of 17 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80
-	20 °C	Elongation of 17 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	Transverse
-	20 °C	Elongation of 17 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Elongation of 18 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	A80
-	20 °C	Elongation of 18 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	Transverse
-	20 °C	Elongation of 18 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Elongation of 19 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	Transverse
-	20 °C	Elongation of 20 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	Transverse
-	20 °C	Elongation of 20 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Elongation of 21 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Elongation of 22 %	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
Hardness, Brinell	-	Hardness, Brinell of 243 [-]	-	-	-	Predicted Value, Transverse
Poisson's ratio	-	Poisson's ratio of 0.29 [-]	-	-	-	Typical for Low Carbon Steel
Reduction of area	-	Reduction of area of 44.0 %	-	-	-	Predicted Value, Transverse
-	-	Reduction of area of 52.7 %	-	-	-	Predicted Value
Shear modulus	-	Shear modulus of 82 GPa	-	-	-	Typical for Low Carbon Steel
Shear strength	-	Shear strength of 513.8 MPa	-	-	-	Predicted Value
Tensile strength	20 °C	Tensile strength of 450 - 680 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Tensile strength of 450 - 630 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Tensile strength of 450 - 600 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Tensile strength of 470 - 680 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Tensile strength of 470 - 630 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Tensile strength of 470 - 600 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Tensile strength of 510 - 680 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Tensile strength of 510 - 630 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Tensile strength of 510 - 600 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
Yield strength	-	Yield strength of 243.9 MPa	-	-	-	Predicted Value, RP1
-	-	Yield strength of 308.5 MPa	-	-	-	Predicted Value, RP1 Transverse
-	-	Yield strength of 367.7 MPa	-	-	-	Predicted Value, Transverse
-	-	Yield strength of 379.8 MPa	-	-	-	Predicted Value, RP05
-	-	Yield strength of 420.8 MPa	-	-	-	Predicted Value, RP02
-	-	Yield strength of 477.7 MPa	-	-	-	Predicted Value, RP02 Transverse
-	-	Yield strength of 480.2 MPa	-	-	-	Predicted Value, RP002
-	20 °C	Yield strength of 265 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Yield strength of 275 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Yield strength of 285 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Yield strength of 295 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Yield strength of 315 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Yield strength of 325 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Yield strength of 335 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Yield strength of 345 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	20 °C	Yield strength of 355 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	Strip, Sheet, Flat, Rod, Wire	-
-	100 °C	Yield strength of 194 - 254 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 194 - 249 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 194 - 234 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 194 - 224 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 194 - 214 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 194 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 214 - 254 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 214 - 249 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 214 - 234 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 214 - 224 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 214 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 224 - 254 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 224 - 249 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 224 - 234 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 224 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 234 - 254 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 234 - 249 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 234 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 249 - 254 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 249 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	100 °C	Yield strength of 254 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 166 - 226 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 166 - 221 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 166 - 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 166 - 196 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 166 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 166 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 186 - 226 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 186 - 221 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 186 - 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 186 - 196 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 196 - 226 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 196 - 221 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 196 - 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 196 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 206 - 226 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 206 - 221 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 221 - 226 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 221 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	200 °C	Yield strength of 226 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 146 - 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 146 - 202 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 146 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 146 - 176 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 146 - 166 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 146 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 166 - 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 166 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 166 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 166 - 202 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 166 - 176 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 176 - 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 176 - 202 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 176 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 176 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 186 - 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 186 - 202 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 202 - 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 202 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	250 °C	Yield strength of 206 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 126 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 126 - 181 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 126 - 166 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 126 - 156 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 126 - 146 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 126 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 146 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 146 - 166 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 146 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 146 - 181 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 146 - 156 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 156 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 156 - 181 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 156 - 166 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 156 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 166 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 166 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 166 - 181 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 181 - 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 181 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-
-	300 °C	Yield strength of 186 MPa	normalized or normalized formed (+N)	EN 10025-2, EN 10025	-	-

Benefit from our expertise in precision engineering to achieve superior steel solutions.

-- Our promise

Similar or equivalent steel materials

Get a quote