EN 10025-2 Grade E335 normalized or normalized formed (+N)
EN 10025-2 Grade E335 normalized or normalized formed (+N) introduction
E335 is a general construction steel. It is applicated for wear and strength loaded construction parts (bolts, shafts, spindles, axles, wedges). The steel is surface hardenable. For this steel (mat. No 1.0543) is available the grade for cold drawing E335GC acc. to DIN EN 10025.
Equivalent material: IS FeE310, IS Fe620, IS E350, IS Fe590, IS SM570, GOST St6ps, GOST St6sp, GOST СT6сп, GOST СT6пс, ASTM A572 Grade 65, DIN St60-2, DIN Fe590-2, DIN 1.0060, EN S335, EN 1.0060, DIN St 60-2, DIN St 60-2 G, DIN E335, AFNOR A60-2, AFNOR E335, UNI Fe590, AISI 450A, BS E335, SAE 450A, JIS SM570, JIS SPFC, ISO Fe590, GB/T HRB335, GB/T L33350
EN 10025-2 Grade E335 normalized or normalized formed (+N) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.85 g/cm³ | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
EN 10025-2 Grade E335 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.08e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Coefficient of thermal expansion of 1.19e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Coefficient of thermal expansion of 1.25e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Coefficient of thermal expansion of 1.3e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Coefficient of thermal expansion of 1.41e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Coefficient of thermal expansion of 1.45e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Coefficient of thermal expansion of 1.49e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Max service temperature | - | Max service temperature of 373.1 °C | - | - | - | Predicted Value, Long |
| - | - | Max service temperature of 500 °C | - | - | - | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | - | - | - | Typical for Low Carbon Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 53.4 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Thermal conductivity of 52.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Thermal conductivity of 50.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Thermal conductivity of 46.7 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Thermal conductivity of 43.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Thermal conductivity of 39.8 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Thermal conductivity of 36.7 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 14.8 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Thermal diffusivity of 13.6 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Thermal diffusivity of 12.1 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Thermal diffusivity of 10.6 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Thermal diffusivity of 9.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Thermal diffusivity of 7.7 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Thermal diffusivity of 6.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
EN 10025-2 Grade E335 normalized or normalized formed (+N) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Nitrogen | Nitrogen of 0.012 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Phosphorus | Phosphorus of 0.045 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Sulfur | Sulfur of 0.045 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
EN 10025-2 Grade E335 normalized or normalized formed (+N) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10025-2 Grade E335 normalized or normalized formed (+N) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 8 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 1.95e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Electrical resistivity of 2.42e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Electrical resistivity of 3.14e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Electrical resistivity of 4.02e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Electrical resistivity of 5.02e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Electrical resistivity of 6.21e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Electrical resistivity of 7.55e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
EN 10025-2 Grade E335 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Elongation | - | Elongation of 14.5 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 20.2 % | - | - | - | Predicted Value, A50 |
| - | - | Elongation of 22.0 % | - | - | - | Predicted Value, A5 |
| - | 20 °C | Elongation of 6 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 7 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 8 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 8 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 9 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 9 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 10 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 10 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 10 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 11 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 11 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 11 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 12 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 13 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Hardness, Brinell | - | Hardness, Brinell of 269 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | 20 °C | Poisson's ratio of 0.284 [-] | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Reduction of area | - | Reduction of area of 42.9 % | - | - | - | Predicted Value, Transverse |
| - | - | Reduction of area of 46.7 % | - | - | - | Predicted Value |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 528.9 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 540 - 770 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 540 - 710 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 550 - 770 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 550 - 710 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 570 - 770 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 570 - 710 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 590 - 770 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 590 - 710 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Yield strength | - | Yield strength of 325 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 329.5 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 331.1 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 332.6 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 423.3 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 494 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 508.5 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 255 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 265 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 275 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 295 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 305 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 315 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 325 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 335 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
We're committed to delivering superior quality and raising the bar in the steel industry.
-- Our promise
Similar or equivalent steel materials
- EN 10025-2 Grade S355J2 normalized or normalized formed (+N)
- EN 10025-2 Grade S275J0 normalized or normalized formed (+N)
- EN 10025-3 Grade S460N normalized or normalized formed (+N)
- ASTM A709 Grade 345 Type 1
- ASTM A709 Grade 345 Type 3
- ASTM A709 Grade 345 Type 2
- EN 10277-2 Grade St60-2 cold drawn
- EN 10277-2 Grade St 60-2 cold drawn or turned and normalized
- EN 10277-2 Grade St 60-2 turned
- EN 10277-2 Grade St 60-2 cold drawn or turned and soft annealed
Get a quote