EN 10025-2 Grade S275J0 normalized or normalized formed (+N)
EN 10025-2 Grade S275J0 normalized or normalized formed (+N) introduction
The hot rolled, unalloyed quality steel S275J0 is a fine grained steel for welding constructions.
The steel is not intended for heat treatment. Stress relieving annealing is allowed. Products in the delivery condition +N may be hot formed and/or normalized after delivery.
For long products and continuous rolled flats the delivery condition is up to the producer +AR, +N or +M. The delivery condition of four-high rolled sheet is also up to the producer and may be +AR or +N. Both conditions can be ordered.
For this steel are available (mat. no 1.0140, S275J0C) grades for folding, roll forming to shape and cold drawing.
Equivalent material: IS Fe410, IS FeE250, IS E275, IS S275C, IS SS400, KS SS400, ASTM A283 Grade D, ASTM A572 Grade 42, ASTM A1011 SS Grade 40, UNS K02702, DIN St44-3U, DIN Fe430C, DIN 1.0143, EN Fe430C, EN 1.0143, DIN St 44-3 U, DIN S275J0, AFNOR E28-3, AFNOR S275J0, UNI Fe430C, UNE AE275C, AISI 290A, AISI 450A, BS 43 C, BS S275J0, SAE 290A, SAE 450A, JIS SS400, JIS SM400B, JIS E275C, ISO S275C, ASTM Grade 345 Type 1, ASTM Grade 345 Type 2, ASTM Grade 345 Type 3
EN 10025-2 Grade S275J0 normalized or normalized formed (+N) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.85 g/cm³ | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
EN 10025-2 Grade S275J0 normalized or normalized formed (+N) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.08e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Coefficient of thermal expansion of 1.19e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Coefficient of thermal expansion of 1.25e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Coefficient of thermal expansion of 1.3e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Coefficient of thermal expansion of 1.41e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Coefficient of thermal expansion of 1.45e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Coefficient of thermal expansion of 1.49e-05 1/K | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Max service temperature | - | Max service temperature of 348.6 °C | - | - | - | Predicted Value, Long |
| - | - | Max service temperature of 500 °C | - | - | - | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | - | - | - | Typical for Low Carbon Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 53.4 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Thermal conductivity of 52.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Thermal conductivity of 50.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Thermal conductivity of 46.7 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Thermal conductivity of 43.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Thermal conductivity of 39.8 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Thermal conductivity of 36.7 W/(m·K) | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 14.8 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Thermal diffusivity of 13.6 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Thermal diffusivity of 12.1 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Thermal diffusivity of 10.6 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Thermal diffusivity of 9.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Thermal diffusivity of 7.7 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Thermal diffusivity of 6.2 mm²/s | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
EN 10025-2 Grade S275J0 normalized or normalized formed (+N) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Copper | Copper of 0.55 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Manganese | Manganese of 1.5 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Nitrogen | Nitrogen of 0.012 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Phosphorus | Phosphorus of 0.03 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
| Sulfur | Sulfur of 0.03 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire |
EN 10025-2 Grade S275J0 normalized or normalized formed (+N) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10025-2 Grade S275J0 normalized or normalized formed (+N) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 7 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 1.95e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Electrical resistivity of 2.42e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Electrical resistivity of 3.14e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Electrical resistivity of 4.02e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Electrical resistivity of 5.02e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Electrical resistivity of 6.21e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Electrical resistivity of 7.55e-07 Ω·m | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
EN 10025-2 Grade S275J0 normalized or normalized formed (+N) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Elongation | - | Elongation of 18.1 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 21.6 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 23.9 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 13 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 14 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 15 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 16 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 Transverse |
| - | 20 °C | Elongation of 17 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 18 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 19 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | A80 |
| - | 20 °C | Elongation of 19 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 19 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 20 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 21 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | Transverse |
| - | 20 °C | Elongation of 21 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 22 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Elongation of 23 % | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Hardness, Brinell | - | Hardness, Brinell of 246 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | 20 °C | Poisson's ratio of 0.284 [-] | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Reduction of area | - | Reduction of area of 43.6 % | - | - | - | Predicted Value, Transverse |
| - | - | Reduction of area of 51 % | - | - | - | Predicted Value |
| Shear modulus | - | Shear modulus of 82 GPa | - | - | - | Typical for Low Carbon Steel |
| Shear strength | - | Shear strength of 490.9 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 380 - 580 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 380 - 560 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 380 - 540 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 400 - 580 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 400 - 560 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 400 - 540 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 410 - 580 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 410 - 560 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 410 - 540 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 430 - 580 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 430 - 560 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Tensile strength of 430 - 540 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| Yield strength | - | Yield strength of 248.3 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 309.7 MPa | - | - | - | Predicted Value, Transverse |
| - | - | Yield strength of 311.8 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 334.5 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 348.6 MPa | - | - | - | Predicted Value, RP02 |
| - | - | Yield strength of 454.9 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 470 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 205 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 215 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 225 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 235 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 245 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 255 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 265 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
| - | 20 °C | Yield strength of 275 MPa | normalized or normalized formed (+N) | EN 10025-2, EN 10025 | Strip, Sheet, Flat, Rod, Wire | - |
Embrace sustainable practices with our eco-friendly steel solutions for a greener future.
-- Our promise
Similar or equivalent steel materials
- EN 10025-2 Grade S275J2 normalized or normalized formed (+N)
- EN 10025-2 Grade S275JR normalized or normalized formed (+N)
- ASTM A709 Grade 345 Type 1
- ASTM A709 Grade 345 Type 3
- ASTM A709 Grade 345 Type 2
- EN 10277-2 Grade St 44-2 cold drawn
- EN 10277-2 Grade St 44-2 cold drawn or turned and normalized
- EN 10277-2 Grade St 44-2 turned
- DIN 2393-2 Grade St 44-2 normalized or normalized formed (+N)
- DIN 2393-2 Grade St 44-2 bright drawn and stress relieved
Get a quote