DIN 17245 Grade GS-17CrMo5-5 quenched and tempered (+QT)
DIN 17245 Grade GS-17CrMo5-5 quenched and tempered (+QT) introduction
GS-17 CrMo 5 5 is used for thick-walled cast pieces at high temperatures and pressures, e.g. for housings, armatures and valve boxes.
Equivalent material: BS B2, UNI G15CrMo55, JIS SCPH21, PN L18HM, STAS T16MoCr11, UNE AM18CrMo05-05, UNE F.8383, MSZ Aö16CrMo, DIN G17CrMo5-5, DIN 1.7357, EN G17CrMo5-5, EN 1.7357, UNS J12072
DIN 17245 Grade GS-17CrMo5-5 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
DIN 17245 Grade GS-17CrMo5-5 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.22E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.34E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.39E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.43E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.46E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of 300 - 610 °C |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 50 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 46 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 42 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 38 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34 W/(m·K) |
- |
DIN 17245 Grade GS-17CrMo5-5 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 - 0.2 % |
| Chromium |
Chromium of 1 - 1.5 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Molybdenum |
Molybdenum of 0.45 - 0.55 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.3 - 0.6 % |
| Sulfur |
Sulfur of 0.015 % |
DIN 17245 Grade GS-17CrMo5-5 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.6E-7 Ω·m |
DIN 17245 Grade GS-17CrMo5-5 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 211 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 204 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 196 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 177 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 164 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 127 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 490 - 640 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 315 MPa |
- |
| Yield strength Rp0.2 |
200.0 °C |
Yield strength Rp0.2 of 255 MPa |
- |
| - |
300.0 °C |
Yield strength Rp0.2 of 230 MPa |
- |
| - |
350.0 °C |
Yield strength Rp0.2 of 215 MPa |
- |
| - |
400.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |
| - |
450.0 °C |
Yield strength Rp0.2 of 190 MPa |
- |
| - |
500.0 °C |
Yield strength Rp0.2 of 180 MPa |
- |
| - |
550.0 °C |
Yield strength Rp0.2 of 160 MPa |
- |
From concept to completion, we deliver excellence in every aspect of the steel supply chain.