EN 10216-2 Grade 12CrMo9-10 quenched and tempered (+QT)
EN 10216-2 Grade 12CrMo9-10 quenched and tempered (+QT) introduction
High temperature steel for high pressure hydrogenation vessels.
Application:
tubes
Equivalent material: EN 12CrMo9-10, DIN 1.7375, BS 12CrMo9-10, JIS SCPH21, JIS SCPH21-CF, JIS SCMQ4V, JIS SFVCMF22B, EN 1.7375, ISO 12CrMo9-10, ISO 13CrMo9-10+NT1, ISO 13CrMo9-10+NT2, ASTM Type A Class 1, ASTM Type A Class 2, ASTM Type A Class 3, ASTM Type A Class 4, ASTM Type A Class 4a, ASTM Grade Type B, ASTM K21590 Class 3, ASTM Grade 22 Cl.4, ASTM Grade 22 Cl.5
EN 10216-2 Grade 12CrMo9-10 quenched and tempered (+QT) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.84 g/cm³ | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
EN 10216-2 Grade 12CrMo9-10 quenched and tempered (+QT) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.05e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 20 °C | Coefficient of thermal expansion of 1.15e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 - 1.22e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Coefficient of thermal expansion of 1.22e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 - 1.29e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Coefficient of thermal expansion of 1.29e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 - 1.34e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Coefficient of thermal expansion of 1.34e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 - 1.4e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Coefficient of thermal expansion of 1.4e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 - 1.43e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Coefficient of thermal expansion of 1.43e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 - 1.46e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Coefficient of thermal expansion of 1.46e-05 1/K | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| Melting point | - | Melting point of 1382 - 1529 °C | - | - | - | Typical for Chromium Molybdenum Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Specific heat capacity of 479 - 500 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Specific heat capacity of 500 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Specific heat capacity of 499 - 540 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Specific heat capacity of 540 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Specific heat capacity of 517 - 580 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Specific heat capacity of 580 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Specific heat capacity of 536 - 620 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Specific heat capacity of 620 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Specific heat capacity of 558 - 690 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Specific heat capacity of 690 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Specific heat capacity of 587 - 780 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Specific heat capacity of 780 J/(kg·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 34.9 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Thermal conductivity of 37 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Thermal conductivity of 37 - 37.3 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Thermal conductivity of 37.3 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Thermal conductivity of 38 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Thermal conductivity of 38 - 38.2 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Thermal conductivity of 38.2 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Thermal conductivity of 37.8 - 38 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Thermal conductivity of 37.8 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Thermal conductivity of 38 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Thermal conductivity of 36.6 - 37 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Thermal conductivity of 36.6 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Thermal conductivity of 37 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Thermal conductivity of 35 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Thermal conductivity of 35 - 35.2 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Thermal conductivity of 35.2 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Thermal conductivity of 33 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Thermal conductivity of 33 - 33.6 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Thermal conductivity of 33.6 W/(m·K) | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 9.7 mm²/s | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Thermal diffusivity of 9.6 mm²/s | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Thermal diffusivity of 9.2 mm²/s | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Thermal diffusivity of 8.5 mm²/s | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Thermal diffusivity of 7.8 mm²/s | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Thermal diffusivity of 6.8 mm²/s | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Thermal diffusivity of 5.7 mm²/s | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
EN 10216-2 Grade 12CrMo9-10 quenched and tempered (+QT) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Aluminium | Aluminium of 0.01 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Carbon | Carbon of 0.1 - 0.15 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Chromium | Chromium of 2 - 2.5 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Copper | Copper of 0.2 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Manganese | Manganese of 0.3 - 0.8 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Molybdenum | Molybdenum of 0.9 - 1.1 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Nickel | Nickel of 0.3 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Phosphorus | Phosphorus of 0.015 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Silicon | Silicon of 0.3 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
| Sulfur | Sulfur of 0.015 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube |
EN 10216-2 Grade 12CrMo9-10 quenched and tempered (+QT) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 3 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 2.98e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Electrical resistivity of 3.4e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Electrical resistivity of 3.4e-07 - 3.43e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Electrical resistivity of 3.43e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Electrical resistivity of 4.1e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Electrical resistivity of 4.1e-07 - 4.13e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Electrical resistivity of 4.13e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Electrical resistivity of 4.97e-07 - 5e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Electrical resistivity of 4.97e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Electrical resistivity of 5e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Electrical resistivity of 5.9e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Electrical resistivity of 5.9e-07 - 5.95e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Electrical resistivity of 5.95e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Electrical resistivity of 7e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Electrical resistivity of 7e-07 - 7.03e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Electrical resistivity of 7.03e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Electrical resistivity of 8.2e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Electrical resistivity of 8.2e-07 - 8.25e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Electrical resistivity of 8.25e-07 Ω·m | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
EN 10216-2 Grade 12CrMo9-10 quenched and tempered (+QT) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 20 °C | Elastic modulus of 212 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Elastic modulus of 207 - 208 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Elastic modulus of 207 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Elastic modulus of 208 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Elastic modulus of 199 - 202 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Elastic modulus of 199 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 200 °C | Elastic modulus of 202 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Elastic modulus of 192 - 194 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Elastic modulus of 192 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 300 °C | Elastic modulus of 194 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Elastic modulus of 184 - 186 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Elastic modulus of 184 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 400 °C | Elastic modulus of 186 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Elastic modulus of 175 - 176 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Elastic modulus of 175 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 500 °C | Elastic modulus of 176 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Elastic modulus of 164 - 166 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Elastic modulus of 164 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 600 °C | Elastic modulus of 166 GPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| Elongation | - | Elongation of 14.9 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 17.0 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 18.0 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 20.4 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 21.0 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 18 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | Transverse |
| - | 20 °C | Elongation of 20 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| Poisson's ratio | - | Poisson's ratio of 0.29 [-] | - | - | - | Typical for Chromium Molybdenum Steel |
| Reduction of area | - | Reduction of area of 46.2 % | - | - | - | Predicted Value, Transverse |
| - | 20 °C | Reduction of area of 50 % | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| Shear modulus | - | Shear modulus of 81.2 GPa | - | - | - | Predicted Value |
| Shear strength | - | Shear strength of 631.8 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 540 - 690 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | Transverse |
| - | 20 °C | Tensile strength of 540 - 690 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | Seamless Tube | - |
| - | 100 °C | Tensile strength of 500 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | - | - |
| - | 150 °C | Tensile strength of 480 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | - | - |
| - | 200 °C | Tensile strength of 460 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | - | - |
| - | 250 °C | Tensile strength of 450 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | - | - |
| - | 300 °C | Tensile strength of 440 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | - | - |
| - | 350 °C | Tensile strength of 430 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | - | - |
| - | 400 °C | Tensile strength of 410 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | - | - |
| - | 450 °C | Tensile strength of 380 MPa | quenched and tempered (+QT) | DIN 17176, EN 10216-2 | - | - |
Partner with us to fuel your growth trajectory, leveraging our reliable supply of high-quality steel for your expanding needs.
-- Our promise
Similar or equivalent steel materials
- EN 10028-2 Grade 10CrMo9-10 normalized and tempered (+NT)
- EN 10028-2 Grade 12CrMo9-10 quenched and tempered (+QT)
- EN 10028-2 Grade 10CrMo9-10 quenched and tempered (+QT)
- ASTM A542 Type A Class 2 Quenched and Tempered
- ASTM A542 Type A Class 1 Quenched and Tempered
- DIN 17155 Grade 10CrMo9-10 quenched and tempered (+QT)
- EN 10273 Grade 10CrMo9-10 normalized and tempered (+NT)
- DIN 17245 Grade GS-17CrMo5-5 quenched and tempered (+QT)
- EN 10273 Grade 10CrMo9-10 normalized and tempered or quenched and tempered