EN 10028-2 Grade 10CrMo9-10 normalized and tempered (+NT)
EN 10028-2 Grade 10CrMo9-10 normalized and tempered (+NT) introduction
Heat-resistant steel for application in pressure vessel and steam boiler construction. Furthermore application for collectors as well as in apparatus engineering and in oil-processing industry.
Max. application temp.: 530 °C
Equivalent material: GB 12Cr2Mo1R, GB A30127, IS 12Cr9Mo10H, IS SCMV4, IS SCMQ4E, KS SCMV4, ASTM A387 Grade 22L, ASTM A387 Grade 22, ASTM A542 Grade A, UNS K21590, DIN 10CrMo9-10, AFNOR 10CD9.10, AFNOR 12CD9.10, BS 622 Grade 31, GOST 12Ch8, IS P34, UNI 12CrMo910, UNI G14CrMo910, IS SFVAF22A, IS SFVAF22B, ÖNORM 10CrMo9-10KW, PN 10H2M, SS 2218, ASTM Grade 22, IS 10CrMo9-10, DIN 1.7380, DIN GS-12CrMo9-10, AFNOR TU 10 CD 9-10A 49-213, BS 1501-622Gr31, BS 45, JIS SPVA, JIS SCMV4, JIS STBA24, JIS SCMQ4E, JIS STPA24, JIS STFA24, JIS SFVCMF22B, EN 1.7380, ISO 10CrMo9-10, ISO 13CrMo9-10+NT1, ISO 13CrMo9-10+NT2, ISO 14CrMo9-10, ASTM Type A Class 1, ASTM Type A Class 2, ASTM Type A Class 3, ASTM Type A Class 4, ASTM Type A Class 4a, ASTM K21590 Class 3, ASTM Grade 22 Cl.4, ASTM Grade 22 Cl.5
EN 10028-2 Grade 10CrMo9-10 normalized and tempered (+NT) general
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
| Density | 20 °C | Density of 7.84 g/cm³ | normalized and tempered (+NT) | EN 10028-2 | Flat |
EN 10028-2 Grade 10CrMo9-10 normalized and tempered (+NT) thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Coefficient of thermal expansion | -100 °C | Coefficient of thermal expansion of 1.05e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Coefficient of thermal expansion of 1.15e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 - 1.22e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.21e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Coefficient of thermal expansion of 1.22e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 - 1.29e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.27e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Coefficient of thermal expansion of 1.29e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 - 1.34e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.32e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Coefficient of thermal expansion of 1.34e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 - 1.4e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.36e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Coefficient of thermal expansion of 1.4e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.4e-05 - 1.43e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Coefficient of thermal expansion of 1.43e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 - 1.46e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Coefficient of thermal expansion of 1.44e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Coefficient of thermal expansion of 1.46e-05 1/K | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Max service temperature | - | Max service temperature of 400 - 550 °C | normalized and tempered (+NT) | EN 10028-2 | Flat | Long |
| Melting point | - | Melting point of 1382 - 1529 °C | - | - | - | Typical for Chromium Molybdenum Steel |
| Specific heat capacity | -100 °C | Specific heat capacity of 423 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 430 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 430 - 461 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Specific heat capacity of 461 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Specific heat capacity of 479 - 500 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Specific heat capacity of 479 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Specific heat capacity of 500 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 - 540 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 499 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Specific heat capacity of 540 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 - 580 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 517 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Specific heat capacity of 580 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 - 620 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 536 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Specific heat capacity of 620 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 558 - 690 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 558 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Specific heat capacity of 690 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Specific heat capacity of 587 - 780 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Specific heat capacity of 587 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Specific heat capacity of 780 J/(kg·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Thermal conductivity | 20 °C | Thermal conductivity of 34.9 - 35 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Thermal conductivity of 34.9 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Thermal conductivity of 35 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 37 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 37 - 37.3 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal conductivity of 37.3 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 38 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 38 - 38.2 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal conductivity of 38.2 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 37.8 - 38 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 37.8 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal conductivity of 38 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 36.6 - 37 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 36.6 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal conductivity of 37 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 35 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 35 - 35.2 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal conductivity of 35.2 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal conductivity of 33 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal conductivity of 33 - 33.6 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal conductivity of 33.6 W/(m·K) | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Thermal diffusivity | 20 °C | Thermal diffusivity of 9.7 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Thermal diffusivity of 9.6 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Thermal diffusivity of 9.2 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Thermal diffusivity of 8.5 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Thermal diffusivity of 7.8 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Thermal diffusivity of 6.8 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Thermal diffusivity of 5.7 mm²/s | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
EN 10028-2 Grade 10CrMo9-10 normalized and tempered (+NT) chemical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
| Carbon | Carbon of 0.08 - 0.14 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Chromium | Chromium of 2 - 2.5 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Copper | Copper of 0.3 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Manganese | Manganese of 0.4 - 0.8 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Molybdenum | Molybdenum of 0.9 - 1.1 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Nitrogen | Nitrogen of 0.012 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Phosphorus | Phosphorus of 0.02 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Silicon | Silicon of 0.5 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
| Sulfur | Sulfur of 0.01 % | normalized and tempered (+NT) | EN 10028-2 | Flat |
EN 10028-2 Grade 10CrMo9-10 normalized and tempered (+NT) electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Electrical conductivity | - | Electrical conductivity of 3 S/m | - | - | - | Predicted Value |
| Electrical resistivity | 20 °C | Electrical resistivity of 2.98e-07 - 3e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Electrical resistivity of 2.98e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Electrical resistivity of 3e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 3.4e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 3.4e-07 - 3.43e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Electrical resistivity of 3.43e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 4.1e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 4.1e-07 - 4.13e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Electrical resistivity of 4.13e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.97e-07 - 5e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 4.97e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Electrical resistivity of 5e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.9e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.9e-07 - 5.95e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Electrical resistivity of 5.95e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 7e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 7e-07 - 7.03e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Electrical resistivity of 7.03e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 8.2e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 8.2e-07 - 8.25e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Electrical resistivity of 8.25e-07 Ω·m | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
EN 10028-2 Grade 10CrMo9-10 normalized and tempered (+NT) mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
| Elastic modulus | -100 °C | Elastic modulus of 217 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212 - 214 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212 - 212.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212.4 - 214 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 212.4 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elastic modulus of 214 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207 - 209 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207 - 207.5 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207.5 - 209 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 207.5 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Elastic modulus of 209 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 199 - 202 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 199 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 199 - 201.2 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 201.2 - 202 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 201.2 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Elastic modulus of 202 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 192 - 195 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 192 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 192 - 193.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 193.9 - 195 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 193.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Elastic modulus of 195 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184 - 187 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 184 - 185.2 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 185.2 - 187 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 185.2 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Elastic modulus of 187 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 174.9 - 177 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 174.9 - 175 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 174.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 175 - 177 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 175 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Elastic modulus of 177 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 163.2 - 167 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 163.2 - 164 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 163.2 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 164 - 167 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 164 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Elastic modulus of 167 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Elongation | - | Elongation of 16.2 % | - | - | - | Predicted Value, A80 |
| - | - | Elongation of 16.4 % | - | - | - | Predicted Value, A80 Transverse |
| - | - | Elongation of 17.8 % | - | - | - | Predicted Value, A200 |
| - | - | Elongation of 20.5 % | - | - | - | Predicted Value, A5 |
| - | - | Elongation of 22 % | - | - | - | Predicted Value, A50 |
| - | 20 °C | Elongation of 17 % | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Elongation of 17 % | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Elongation of 18 % | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Elongation of 18 % | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Hardness, Brinell | - | Hardness, Brinell of 227 [-] | - | - | - | Predicted Value, Transverse |
| Poisson's ratio | 20 °C | Poisson's ratio of 0.283 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Poisson's ratio of 0.286 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Poisson's ratio of 0.292 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Poisson's ratio of 0.294 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Poisson's ratio of 0.3 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Poisson's ratio of 0.307 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Poisson's ratio of 0.313 [-] | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Reduction of area | - | Reduction of area of 42.1 % | - | - | - | Predicted Value |
| - | - | Reduction of area of 45.7 % | - | - | - | Predicted Value, Transverse |
| Shear modulus | 20 °C | Shear modulus of 82.8 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 100 °C | Shear modulus of 80.7 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 200 °C | Shear modulus of 77.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 300 °C | Shear modulus of 74.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 400 °C | Shear modulus of 71.2 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 500 °C | Shear modulus of 66.9 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 600 °C | Shear modulus of 62.1 GPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Shear strength | - | Shear strength of 604 MPa | - | - | - | Predicted Value |
| Tensile strength | 20 °C | Tensile strength of 470 - 630 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 470 - 620 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 470 - 630 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 470 - 620 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 480 - 630 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 480 - 620 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Tensile strength of 480 - 630 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Tensile strength of 480 - 620 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| Yield strength | - | Yield strength of 260.9 MPa | - | - | - | Predicted Value, RP1 |
| - | - | Yield strength of 266.1 MPa | - | - | - | Predicted Value, RP1 Transverse |
| - | - | Yield strength of 380.7 MPa | - | - | - | Predicted Value, RP05 |
| - | - | Yield strength of 382 MPa | - | - | - | Predicted Value, RP02 Transverse |
| - | - | Yield strength of 485.8 MPa | - | - | - | Predicted Value, RP002 |
| - | 20 °C | Yield strength of 280 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Yield strength of 280 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Yield strength of 290 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Yield strength of 290 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Yield strength of 300 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Yield strength of 300 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 20 °C | Yield strength of 310 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | Transverse |
| - | 20 °C | Yield strength of 310 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | - |
| - | 50 °C | Yield strength of 260 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 50 °C | Yield strength of 270 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 50 °C | Yield strength of 279 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 50 °C | Yield strength of 288 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 100 °C | Yield strength of 240 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 100 °C | Yield strength of 249 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 100 °C | Yield strength of 257 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 100 °C | Yield strength of 266 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 150 °C | Yield strength of 230 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 150 °C | Yield strength of 238 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 150 °C | Yield strength of 246 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 150 °C | Yield strength of 254 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 200 °C | Yield strength of 224 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 200 °C | Yield strength of 232 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 200 °C | Yield strength of 240 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 200 °C | Yield strength of 248 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 250 °C | Yield strength of 220 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 250 °C | Yield strength of 227 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 250 °C | Yield strength of 235 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 250 °C | Yield strength of 243 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 300 °C | Yield strength of 213 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 300 °C | Yield strength of 221 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 300 °C | Yield strength of 228 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 300 °C | Yield strength of 236 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 350 °C | Yield strength of 204 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 350 °C | Yield strength of 211 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 350 °C | Yield strength of 218 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 350 °C | Yield strength of 225 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 400 °C | Yield strength of 191 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 400 °C | Yield strength of 198 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 400 °C | Yield strength of 205 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 400 °C | Yield strength of 212 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 450 °C | Yield strength of 178 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 450 °C | Yield strength of 185 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 450 °C | Yield strength of 191 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 450 °C | Yield strength of 197 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 500 °C | Yield strength of 167 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 500 °C | Yield strength of 173 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 500 °C | Yield strength of 179 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
| - | 500 °C | Yield strength of 185 MPa | normalized and tempered (+NT) | EN 10028-2 | Flat | RP02 |
Experience the strength, resilience, and versatility of our premium steel products.
-- Our promise
Similar or equivalent steel materials
- EN 10028-2 Grade 12CrMo9-10 quenched and tempered (+QT)
- EN 10028-2 Grade 10CrMo9-10 quenched and tempered (+QT)
- EN 10216-2 Grade 12CrMo9-10 quenched and tempered (+QT)
- ASTM A542 Type A Class 2 Quenched and Tempered
- ASTM A542 Type A Class 1 Quenched and Tempered
- DIN 17155 Grade 10CrMo9-10 quenched and tempered (+QT)
- EN 10273 Grade 10CrMo9-10 normalized and tempered (+NT)
- EN 10273 Grade 10CrMo9-10 normalized and tempered or quenched and tempered
- EN 10216-2 Grade 11CrMo9-10 quenched and tempered (+QT)
- EN 10222-2 Grade 11CrMo9-10 normalized and tempered (+NT)
Get a quote