ASTM A533 Type A Class 1 Quenched and Tempered
Equivalent material: DIN 1.7375, DIN 12CrMo9-10, BS 12CrMo9-10, JIS SCPH21, JIS SCPH21-CF, JIS SCMQ4V, JIS SFVCMF22B, EN 12CrMo9-10, EN 1.7375, ISO 12CrMo9-10, ISO 13CrMo9-10+NT1, ISO 13CrMo9-10+NT2, ASTM Type A Class 2, ASTM Type A Class 3, ASTM Type A Class 4, ASTM Type A Class 4a, ASTM Grade Type B, ASTM K21590 Class 3, ASTM Grade 22 Cl.4, ASTM Grade 22 Cl.5, DIN 1.7380, DIN GS-12CrMo9-10, DIN 10CrMo9-10, AFNOR TU 10 CD 9-10A 49-213, BS 1501-622Gr31, BS 45, JIS SPVA, JIS SCMV4, JIS STBA24, JIS SCMQ4E, JIS STPA24, JIS STFA24, EN 10CrMo9-10, EN 1.7380, ISO 10CrMo9-10, ISO 14CrMo9-10, GOST 12Ch8, DIN 1.7383, DIN 11CrMo9-10, BS 11CrMo9-10, JIS SFVAF22A, JIS SFVAF22B, EN 11CrMo9-10, EN 1.7383
ASTM A533 Type A Class 1 Quenched and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Molybdenum Steel |
ASTM A533 Type A Class 1 Quenched and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.4E-5 1/K |
Typical for Chromium Molybdenum Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 448 - 502 J/(kg·K) |
Typical for Chromium Molybdenum Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 - 43 W/(m·K) |
Typical for Chromium Molybdenum Steel |
ASTM A533 Type A Class 1 Quenched and Tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.25 % |
| Manganese |
Manganese of 1.15 - 1.5 % |
| Molybdenum |
Molybdenum of 0.45 - 0.6 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.4 % |
| Sulfur |
Sulfur of 0.025 % |
ASTM A533 Type A Class 1 Quenched and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Molybdenum Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 18 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 550 - 690 MPa |
- |