ASTM A769 Grade 60
Equivalent material: DIN 1.0487, DIN WStE 285, DIN P275NH, AFNOR P275NH, BS 224-400B, BS P275NH, AISI 290A, SAE 290A, EN P275NH, EN 1.0487, ISO P275NH, DIN 1.0523, DIN S430GP, AFNOR S430GP, BS S430GP, EN S430GP, EN 1.0523
ASTM A769 Grade 60 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A769 Grade 60 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A769 Grade 60 chemical
| Property |
Value |
| Carbon |
Carbon of 0.26 % |
| Manganese |
Manganese of 0.3 - 1.65 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.035 % |
ASTM A769 Grade 60 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A769 Grade 60 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A769 Grade 60 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A200 |
23.0 °C |
Elongation A200 of 12 % |
- |
| Elongation A50 |
23.0 °C |
Elongation A50 of 17 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 415 MPa |
- |